Stabilization of refining slags by correction of their phase composition
- Авторы: Sheshukov O.1,2, Nekrasov I.1, Mikheenkov M.1, Egnazar’yan D.1, Ovchinnikova L.1
-
Учреждения:
- Institute of Metallurgy, Ural Branch
- Yeltsin Ural Federal University
- Выпуск: Том 46, № 5 (2016)
- Страницы: 339-342
- Раздел: Article
- URL: https://journals.rcsi.science/0967-0912/article/view/178725
- DOI: https://doi.org/10.3103/S0967091216050120
- ID: 178725
Цитировать
Аннотация
The stabilization of refining slags in ladle treatment with alumina fluxes is studied. In refining, the slag is stabilized in the presence of alumina fluxes thanks to isomorphic replacement of a calcium ion by alkali-metal ions and to decrease in the dicalcium-silicate content in the melt as a result of its replacement by aluminum-bearing phases.
Ключевые слова
Об авторах
O. Sheshukov
Institute of Metallurgy, Ural Branch; Yeltsin Ural Federal University
Автор, ответственный за переписку.
Email: silast@mail.ru
Россия, Yekaterinburg; Yekaterinburg
I. Nekrasov
Institute of Metallurgy, Ural Branch
Email: silast@mail.ru
Россия, Yekaterinburg
M. Mikheenkov
Institute of Metallurgy, Ural Branch
Email: silast@mail.ru
Россия, Yekaterinburg
D. Egnazar’yan
Institute of Metallurgy, Ural Branch
Email: silast@mail.ru
Россия, Yekaterinburg
L. Ovchinnikova
Institute of Metallurgy, Ural Branch
Email: silast@mail.ru
Россия, Yekaterinburg