Morphology of the γ → α recrystalllization front with diffusional change in composition of complex iron alloys
- Autores: Gubenko S.1, Sychkov A.2, Chernoivanenko E.1
-
Afiliações:
- Ukrainian National Metallurgical Academy
- Nosov Magnitogorsk State Technical University
- Edição: Volume 47, Nº 5 (2017)
- Páginas: 349-352
- Seção: Article
- URL: https://journals.rcsi.science/0967-0912/article/view/179630
- DOI: https://doi.org/10.3103/S0967091217050059
- ID: 179630
Citar
Resumo
The formation of the phase-transformation front in complex iron alloys during decarburization is studied. The influence of the main alloying element (tungsten) on the morphology of the recrystallization front in γ + Me6C → α transformation is analyzed; this transformation is responsible for diffusional change in composition in isothermal conditions.
Sobre autores
S. Gubenko
Ukrainian National Metallurgical Academy
Email: absychkov@mail.ru
Ucrânia, Dnepr
A. Sychkov
Nosov Magnitogorsk State Technical University
Autor responsável pela correspondência
Email: absychkov@mail.ru
Rússia, Magnitogorsk
E. Chernoivanenko
Ukrainian National Metallurgical Academy
Email: absychkov@mail.ru
Ucrânia, Dnepr