Morphology of the γ → α recrystalllization front with diffusional change in composition of complex iron alloys
- Authors: Gubenko S.I.1, Sychkov A.B.2, Chernoivanenko E.A.1
-
Affiliations:
- Ukrainian National Metallurgical Academy
- Nosov Magnitogorsk State Technical University
- Issue: Vol 47, No 5 (2017)
- Pages: 349-352
- Section: Article
- URL: https://journals.rcsi.science/0967-0912/article/view/179630
- DOI: https://doi.org/10.3103/S0967091217050059
- ID: 179630
Cite item
Abstract
The formation of the phase-transformation front in complex iron alloys during decarburization is studied. The influence of the main alloying element (tungsten) on the morphology of the recrystallization front in γ + Me6C → α transformation is analyzed; this transformation is responsible for diffusional change in composition in isothermal conditions.
About the authors
S. I. Gubenko
Ukrainian National Metallurgical Academy
Email: absychkov@mail.ru
Ukraine, Dnepr
A. B. Sychkov
Nosov Magnitogorsk State Technical University
Author for correspondence.
Email: absychkov@mail.ru
Russian Federation, Magnitogorsk
E. A. Chernoivanenko
Ukrainian National Metallurgical Academy
Email: absychkov@mail.ru
Ukraine, Dnepr