Отправить статью по E-mail Investigation of Cutting Ceramic Stability During Sharpening of Hardened Steel Blanks
- Авторы: Pronin A.I.1, Myl’nikov V.V.2, Shchelkunov E.B.1, Chernyshov E.A.3
-
Учреждения:
- Komsomolsk-on-Amur State Technical University
- Nizhegorodskii State Architecture and Construction University
- R. E. Alekseev Nizhegorodskii State Technical University
- Выпуск: Том 74, № 9-10 (2018)
- Страницы: 364-366
- Раздел: Article
- URL: https://journals.rcsi.science/0361-7610/article/view/245068
- DOI: https://doi.org/10.1007/s10717-018-9995-7
- ID: 245068
Цитировать
Открытый доступ
Доступ предоставлен
Только для подписчиков
Аннотация
The results of investigations of the stability of VOK-60 cutting ceramic during machining of hardened steel blanks made of No. 45 steel of different hardness 45 HRC and 54 HRC are presented. The stability of the cutting ceramic plate during machining of a harder blank is 41% higher than in machining of a less-hard blank. A microstructural analysis of the damage to the working surface was performed and the mechanism of wear of the cutting plate was determined. The reasons for the more rapid wear of the plate during machining of a less-hard blank were determined.
Об авторах
A. Pronin
Komsomolsk-on-Amur State Technical University
Email: mrmylnikov@mail.ru
Россия, Komsomolskon-Amur
V. Myl’nikov
Nizhegorodskii State Architecture and Construction University
Автор, ответственный за переписку.
Email: mrmylnikov@mail.ru
Россия, Nizhny Novgorod
E. Shchelkunov
Komsomolsk-on-Amur State Technical University
Email: mrmylnikov@mail.ru
Россия, Komsomolskon-Amur
E. Chernyshov
R. E. Alekseev Nizhegorodskii State Technical University
Email: mrmylnikov@mail.ru
Россия, Nizhny Novgorod
Дополнительные файлы