Мақаланы E-mail арқылы жіберу Glass Ceramic Materials Based on Beneficiation Tailings of Lead-Zinc Ore
- Авторлар: Pavlov M.V.1, Pavlov I.V.1, Lineitsev A.V.2, Pavlov V.F.3
-
Мекемелер:
- NAUKA Special Design and Technological Office, Siberian Branch of the Russian Academy of Sciences
- Institute of Non-ferrous Metals and Materials Science, Siberian Federal University
- Krasnoyarsk Scientific Center, Siberian Branch of the Russian Academy of Sciences
- Шығарылым: Том 73, № 11-12 (2017)
- Беттер: 459-464
- Бөлім: Wastes—Into Production
- URL: https://journals.rcsi.science/0361-7610/article/view/244751
- DOI: https://doi.org/10.1007/s10717-017-9911-6
- ID: 244751
Дәйексөз келтіру
Ашық рұқсат
Рұқсат берілді
Тек жазылушылар үшін
Аннотация
A glass ceramic material was obtained from the beneficiation tailings of lead-zinc ores. The strength of the control samples was 22.26 MPa in bending and 90.22 MPa in compression. After 100 cycles of testing the samples for frost resistance, these characteristics changed to 9.61 MPa in bending and 35.30 MPa in compression.
Авторлар туралы
M. Pavlov
NAUKA Special Design and Technological Office, Siberian Branch of the Russian Academy of Sciences
Email: pavlov@akadem.ru
Ресей, Krasnoyarsk
I. Pavlov
NAUKA Special Design and Technological Office, Siberian Branch of the Russian Academy of Sciences
Email: pavlov@akadem.ru
Ресей, Krasnoyarsk
A. Lineitsev
Institute of Non-ferrous Metals and Materials Science, Siberian Federal University
Email: pavlov@akadem.ru
Ресей, Krasnoyarsk
V. Pavlov
Krasnoyarsk Scientific Center, Siberian Branch of the Russian Academy of Sciences
Хат алмасуға жауапты Автор.
Email: pavlov@akadem.ru
Ресей, Krasnoyarsk
Қосымша файлдар