LOW-TEMPERATURE ELECTROLYTIC PRODUCTION OF Al-REM ALLOYS IN CRYOLITE MELTS

A. V. Rudenko; Руденко А. В.; O. Yu. Tkacheva; Ткачева О. Ю.; A. A. Kataev; Катаев А. А.

doi:10.31857/S0235010623040060

LOW-TEMPERATURE ELECTROLYTIC PRODUCTION OF Al-REM ALLOYS IN CRYOLITE MELTS

Autores: Rudenko A.¹, Tkacheva O.¹, Kataev A.¹
Afiliações:
1. Institute of High Temperature Electrochemistry, Ural Branch of the RAS
Edição: Nº 4 (2023)
Páginas: 385-395
Seção: Articles
URL: https://journals.rcsi.science/0235-0106/article/view/138734
DOI: https://doi.org/10.31857/S0235010623040060
EDN: https://elibrary.ru/XFTAJK
ID: 138734

Citar

Texto integral

Acesso aberto
Acesso é fechado

Acesso está concedido
Acesso é fechado

Somente assinantes

Resumo
Sobre autores
Bibliografia
Arquivos suplementares
Estatísticas

Resumo

The process of electrolytic production of Al–Y and Al–Sc alloys in an electrolyte based on potassium cryolite KF–NaF(10 wt %)–AlF₃ with a cryolite ratio (CR) of 1.5, containing Al₂O₃, Sc₂O₃, or Y₂O₃ oxides, in a cell with vertical electrodes has been studied. The Fe–Ni–Cu alloy served as an inert anode. The wetted cathode was a graphite plate coated with the aluminum diboride. The electrolysis was carried out at a cathode current density of 0.2 A/cm² and a temperature of 830°C. The Al₂O₃ mass was calculated based on the value of the current efficiency of 60%. The Sc₂O₃ additive was introduced into the melt in an amount of 1 wt %. The mass of the Y₂O₃ additive was chosen based on its solubility in the melt under study. For this, the influence of Y₂O₃ additives on the liquidus temperature of the quasi-binary mixture [KF–NaF(10 wt %)–AlF₃ (KO = 1.5)]–Y₂O₃ was determined and it was found that, in contrast to Sc₂O₃ additives, which lower the liquidus temperature of the cryolite melt, small additions of Y₂O₃ lead to its sharp increase. It has been found that the efficiency of the electrolytic reduction of Y₂O₃ is 10 times higher than that of the aluminothermic reduction. Other things being equal, the efficiency of the electrolytic reduction of Y₂O₃ is higher than that of Sc₂O₃. Alloys Al–Y and Al–Sc with a REM content of 0.6 wt % have been obtained. However, the time to reach the maximum recovery of yttrium significantly exceeds the time to recover scandium. Metallographic studies of the obtained alloys indicated the presence of Al₃Sc and Al₂Y intermetallic compounds. A conclusion is made about the fundamental possibility of low-temperature electrolytic production of Al-REM alloys in cryolite melts based on potassium cryolite in vertical cells with an inert metal anode and a wettable cathode.

Palavras-chave

cryolite, melts, cryolite ratio, yttrium oxide, scandium oxide

Bibliografia

Ri E. Kh., Ri Kh., Goncharov A.V. Effect of Al–Y–Ce–La master alloy on structure formation, liquation processes and properties of AK7ch silumine (Al9) // MATEC Web of Conferences. 2019. 298.
Zou H., Zeng X., Zhai C., Ding W. The effects of yttrium element on microstructure and mechanical properties of Mg–5 wt % Zn–2 wt % Al alloy // Materials Science and Engineering A. 2005. 402. P. 142–148.
Huang K., Feng Q., Zhou W., Ren Y., Huang L., Xiang J., Tang H., Zhu Y., Wei Y. Enhancement of strength mechanical and corrosion resistance of 7055 alloy with minor Sc and Y addition // Mater. Res. Express 8. 2021. № 016524.
Nikitin V.I., Krivopalov D.S., Nikitin K.V., Napalkov V.I., Makhov S.V. Vliyaniye usloviy kristallizatsii na strukturu modifitsiruyushchey ligatury A–Sc [Influence of crystallization conditions on the structure of the modifying master alloy A-Sc] // Liteynoye proizvodstvo. 2014. № 11. P. 5–8. [In Russian].
Chen Y., Liu C.Y., Ma Z.Y., Huang H.F., Peng Y.H., Hou Y.F. Effect of Sc addition on the microstructure, mechanical properties, and damping capacity of Al–20Zn alloy // Materials characterization. 2019. 159. P. 109892.
Prach O., Trudonoshyn O., Randelzhofer P., Körner С., Durst K. Effect of Zr, Cr and Sc on the Al–Mg–Si–Mn high-pressure die casting alloys // Materials Science & Engineering A. 2019. 459. P. 603–612.
Liao W., Jiang W., Yang X.-Sh., Wang H., Ouyang L., Zhu M. Enhancing (de) hydrogenation kinetics properties of the Mg/MgH2 system by adding ANi5 (A 1/4 Ce, Nd, Pr, Sm, and Y) alloys via ball milling // J. Rare Earths. 2021. 39. P. 1010–1016.
Skachkov V.M., Yatsenko S.P. Polucheniye Sc, Zr, Hf, Y ligatur na osnove alyuminiya metodom vysokotemperaturnykh obmennykh reaktsiy v rasplavakh soley [Obtaining Sc, Zr, Hf, Y master alloys based on aluminum by the method of high-temperature exchange reactions in molten salts] // Tsvetnyye metally. 2014. № 3. P. 22–26. [In Russian].
Konokotin S.P., Yatsyuk I.V., Dobrynin D.A., Azarovskiy Ye.N. Vliyaniye ittriya na kachestvo litykh zagotovok iz splavov na osnove alyuminiya [Influence of yttrium on the quality of cast billets from aluminum-based alloys] // Nauchno-tekhnicheskiy zhurnal “Trudy VAMI”. 2020. № 3. [In Russian].
Snitovskiy Yu.P. Fazovyy sostav i kontsentratsii ittriya v plenkakh pri osazhdenii alyuminiya i alyuminiyevykh splavov iz gazovoy fazy [Phase composition and concentrations of yttrium in films during the deposition of aluminum and aluminum alloys from the gas phase] // Vestnik Yugorskogo gosudarstvennogo universiteta. 2021. 4. № 63. P. 16–31. [In Russian].
Makhov S.V., Moskvitin V.I. Sovremennaya tekhnologiya polucheniya alyuminiyevo-skandiyevoy ligatury [Modern technology for obtaining aluminum-scandium ligatures] // Tsvetnyye metally. 2010. № 5. P. 95–96. [In Russian].
He J., Hua Zh., Liu H., Xu L., He Sh., Yang Y., Zhao Zh. Redox behavior of yttrium and electrochemical formation of Y–Al alloys in molten chlorides // J. Electrochem. Soc. 2018. 165. № 11. P. 598–603.
Yan Y.D., Yang X.N., Huang Y., Xue Y., Zhang M.L., Han W., Zhang Zh. Direct electrochemical formation of different phases Al–Y alloys by co-deposition in LiCl–KCl melts // Rare Met Mater Eng. 2016. 45. № 2. P. 272.
Yu G., Zhou L., Liu F., Pang S., Chen D., Zhao H., Zuo Zh. Electrochemical co-reduction of Y(III) and Al(III) in a fluoride molten salt system and electrolytic preparation of Y–Al intermediate alloys // J. Rare Earths. 2022. 40. № 8. P. 1945–1952.
Filatov A.A., Nikolaev A.Y., Suzdaltsev A.V., Zaikov Y.P. Extraction of zirconium from its oxide during electrolysis of the KF–AlF3–Al2O3–ZrO2 melts // Russian J. Non-Ferrous Metals. 2022. 63. № 4. P. 379–384.
Filatov A., Suzdaltsev A., Zaikov Y. Production of Al–Zr master alloy by electrolysis of the KF–NaF–AlF3–ZrO2 melt: modifying ability of the master alloy // Metallurgical and Materials Transactions B: Process Metallurgy and Materials Processing Science. 2021. 52. № 6. P. 4206–4214.
Nikolayev A.Yu., Suzdal’tsev A.V., Zaykov Yu.P. Elektrovydeleniye alyuminiya i skandiya iz ftoridnykh i oksidno-ftoridnykh rasplavov [Electrical release of aluminum and scandium from fluoride and oxide-fluoride melts] // Butlerovskiye soobshcheniya. 2018. 56. № 10. P. 75–83. [In Russian].
Nikolaev A.Yu., Suzdaltsev A.V., Zaikov Yu.P. Electrowinning of aluminium and scandium from KF–AlF3–Sc2O3 melts for the synthesis of Al–Sc master alloys // J. Electrochemical Society. 2019. 166. № 8. P. D252–D257.
Nikolayev A.Yu., Suzdal’tsev A.V., Zaykov Yu.P. Novyy sposob sinteza ligatur Al–Sc v oksidno-ftoridnykh i ftoridnykh rasplavakh [A new method for the synthesis of Al–Sc master alloys in oxide-fluoride and fluoride melts] // Rasplavy. 2020. № 2. P. 155–165. [In Russian].
Suzdaltsev A.V., Filatov A.A., Nikolaev A.Yu., Pankratov A.A., Molchanova N.G., Zaikov Yu.P. Extraction of scandium and zirconium from their oxides during the electrolysis of oxide–fluoride melts // Russian Metallurgy. 2018. № 2. P. 133–138.
Report of the American Society of Mechanical Engineers. Technical Working Group on Inert Anode Technologies. The U.S. Department of Energy Office of Industrial Technologies. CRTD – Vol. 53. 1999.
Dedyukhin A.Ye., Apisarov A.P., Tkacheva O.Yu., Red’kin A.A., Zaykov Yu.P., Frolov A.V., Gusev A.O. Vliyaniye NaF na elektroprovodnost’ i temperaturu likvidusa rasplavlennoy sistemy KF–AlF3 [Influence of NaF on the electrical conductivity and liquidus temperature of the molten KF–AlF3 system] // Rasplavy. 2008. № 4. P. 44–50. [In Russian].
Yasinskiy A.S., Padamata S.K., Polyakov P.V., Shabanov A.V. An update on inert anodes for aluminium electrolysis // Non-ferrous Metals. 2020. № 1. P. 15–23.
Rudenko A.V., Kataev A.A., Neupokoeva M.M., Tkacheva O.Y. Borated graphite cathodes for low-temperature aluminum electrolysis // Chimica Techno Acta. 2022. 9. № 2. P. 20229208.
Rudenko A.V., Katayev A.A., Zakir’yanova I.D., Tkacheva O.Yu. Vliyaniye Sc2O3 na fiziko-khimicheskiye svoystva legkoplavkikh kriolitovykh rasplavov KF–AlF3 i KF–NaF–AlF3 [Effect of Sc2O3 on the physicochemical properties of low-melting cryolite melts KF–AlF3 and KF–NaF–AlF3] // Tsvetnyye metally. 2017. № 11. P. 22–26. [In Russian].
Suzdaltsev A.V., Filatov A.A., Nikolaev A.Yu., Pankratov A.A., Molchanova N.G., Zaikov Yu.P. Extraction of scandium and zirconium from their oxides during the electrolysis of oxide–fluoride melts // Russian Metallurgy. 2018. № 2. P. 133–138.