Nondestructive evaluation by eddy current and ultrasonic technique of 475�C embrittlement effects in dss duplex stainless steels and corrosion behavior

Capa

Citar

Texto integral

Acesso aberto Acesso aberto
Acesso é fechado Acesso está concedido
Acesso é fechado Somente assinantes

Resumo

In this paper, a non-destructive evaluation of the embrittlement effect in duplex stainless steel DSS 2205 aged from 5 h to 100 h at a temperature of 475 ° C was performed by Eddy current and ultrasonic techniques, in addition the corrosion behavior was carried out after heat treatment at 475°C. The experimental results show that an inverse behavior was observed between normalized impedance and hardness in aging time at 475°C; when the normalized impedance of the Eddy current probe was decreased, hardness was increased with aging time. The longitudinal ultrasonic velocity and transversal velocity were calculated in this study for each sample. The Young’s modulus and the Shear modulus were computed from the two velocities. The investigation carried out shows a sensitivity of Eddy current and ultrasonic technique to the microstructure changing observed at 475 ° C, due to embrittlement in duplex stainless steel. The effect of heat treatment at 475°C on the corrosion behavior was also evaluated by Eddy current on a long time and revealed the important changing in corrosion resistance due to spinodale decomposition of the ferrite phase.

Sobre autores

R. Ghis

Laboratory of Materials and Energies, Institute of Sciences and Technology, University Center of Tamanrasset

Email: rimghis21@gmail.com
Tamanrasset, Algeria

A. Hammouda

Research Center in Industrial Technologies (CRTI)

Cheraga, Algeria

A. Ziouche

Research Center in Industrial Technologies (CRTI)

Cheraga, Algeria

N. Boucherou

Research Center in Industrial Technologies (CRTI)

Cheraga, Algeria

A. Choucha

Laboratory of Materials and Energies, Institute of Sciences and Technology, University Center of Tamanrasset

Tamanrasset, Algeria

R. Halimi

Research Center in Industrial Technologies (CRTI)

Cheraga, Algeria

A. Benmoussat

Laboratory of Materials and Energies, Institute of Sciences and Technology, University Center of Tamanrasset

Tamanrasset, Algeria

Bibliografia

  1. Argandona G., Biezma M.V., Berrueta J.M., Berlanga C., Ruiz A. Detection of Secondary Phases in UNS S32760 Superduplex Stainless Steel by Destructive and Non-destructive Techniques // Journal of Materials Engineering and Performance. 2016. V. 25. P. 5269-79.
  2. Nilsson J.-O. Super duplex stainless steels // Materials Science and Technology. 1992. V. 8. P. 685-700.
  3. Gunn R.N. Duplex stainless steels: microstructure, properties and applications. Woodhead Publishing, 1997.
  4. Lo K.H., Shek C.H., Lai J. Recent developments in stainless steels // Materials Science and Engineering. R: Reports. 2009. V. 65. P. 39-104.
  5. Chung H.M.International Journal of Pressure Vessels and Piping. 1992. V. 50. P. 179-213.
  6. Reidrich G., Loib F. Embrittlement of high chromium steels within temperature range of 570-1100 °F // ArchivFür Das Eisenhüttenwesen. 1941. V. 15. P. 175-82
  7. Olsson J., Liljas M. 60 years of duplex stainless steel applications / Proceedings from NACE Corrosion'94. Paper No 395. Baltimore, Maryland, USA, 1994.
  8. Charles J. Super duplex stainless steels: structure and properties // Proceedings of Conference Duplex Stainless Steels′91, Beaune Bourcogne, France, 1991. P. 3-48.
  9. Solomon H.D., Levinson L.M. Mössbauer effect study of "475 °C embrittlement" of duplex and ferritic stainless steels // Acta Metallurgica. 1978. V. 26. P. 429-42.
  10. Tsuchiya S., Ishikawa Y., Ohtaka M., Yoshimura T. JSME International Journal Series A. 1995. V. 38. P. 384.
  11. Evanson S., Otaka M., Hasegawa K.J. Engineering Mater. and Technology. 1992. V. 114. P. 42.
  12. Maeda N., Goto T., Nakamura T., Naito T., Kumano S., Nakao Y.Int. J. Pres. Ves. & Piping. 1997. V. 71. P. 7.
  13. Gutiérrez-Vargas G., López-Morelos V.H., Carreón H., Kim J.Y., Ruiz A. ACPD detection and evaluation of 475°C embrittlement of aged 2507 super duplex stainless steels / AIP conference procedings 2017. V. 1806. P. 110018.
  14. Gutiérrez-Vargas G., Ruiz A., Kim J.Y., López-Morelos V.H., Ambriz R.R. Evaluation of thermal embrittlement in 2507 super duplex stainless steel using thermoelectric power // Nucl. Eng. Technol. 2019. V. 51. P. 1816-1821.
  15. Camerini C., Sacramento R., Areiza M.C., Rocha A., Santos R., Rebello J.M., Pereira G. Eddy Current Techniques for Super Duplex Stainless Steel Characterization //j. Magn. Magn. Mater. 2015. V. 388. P. 96-100.
  16. Ziouche A., Zergoug M., Boucherou N., Boudjellal H,; Mokhtari M., Abaidia S. Pulsed Eddy Current Signal Analysis of Ferrous and Non-Ferrous Metals under Thermal and Corrosion Solicitations // Russian Journal of Nondestructive Testing. 2017. V. 53. No. 9. P. 652-659.
  17. Ziouche A., Haddad A., Badji R., Zergoug M., Zoubiri N., Bedjaoui W., Abaidia S. Microstructure, Corrosion and Magnetic Behavior of an Aged Dual-Phase Stainless Steel //j. Materials Engineering and Performance. 2018.
  18. Araújo Freitas V.L., Normando P.G., Albuquerque V.H.C., Silva E. Macedo, Silva A.A., Tavares J.M.R.S. Nondestructive characterization and evaluation of embrittlement kinetics and elastic constants of duplex stainless steel SAF 2205 for different aging times at 425°C and 475°C //j. Alloys Compd. 2011. V. 30. P. 130-136.
  19. Redjaimia A., Morniroli J.P., Donnadieu P., Metauer G. Microstructural and Analytical Study of Heavily Faulted Frank-Kasper R-Phase Precipitates in the Ferrite of a Duplex Stainless Steel //j. Mater. Sci. 2002. V. 37. No. 19. P. 4079-4091.
  20. Örnek C., Burke M.G., Hashimoto T., Lim J.J.H., D. L. 475° C embrittlement of duplex stainless steel - a comprehensive microstructure characterization study Engelberg // Materials Performance Characterization. 2017. V. 6 (4).
  21. Pareige C., Emo J., Saillet S., Domain C., Pareige P. Kinetics of G-phase precipitation and spinodal decomposition in very long aged ferrite of a Mo-free duplex stainless steel // Journal of Nuclear Materials. 2015. V. 465. P. 383-389.
  22. Zergoug M. et al. Relation between mechanical microhardness and impedance variations in Eddy current testing // NDT&E Int. 2004. V. 37. P. 65-67.
  23. Tavares S.S.M., de Noronha R.F., da Silva M.R., Neto J.M., Pairis S. 475_C Embrittlement in a Duplex Stainless Steel UNS S31803 // Mater. Res. 2001. V. 4. No. 4. P. 237-240.
  24. Silva E.M., Albuquerque V.H.C., Leite J.P., Varela A.C.G., Moura E.P., Tavares J.M.R.S. Phase on a UNS S31803 duplex stainless steel based on nondestructive testing // Mater. Sci. Eng. A. 2009. V. 516. P. 126-130.
  25. Lekbir C., Dahoun N., Guetitech A. et al. Effect of Immersion Time and Cooling Mode on the Electrochemical Behavior of Hot-Dip Galvanized Steel in Sulfuric Acid Medium // Journal of Materials Engineering and Performance. 2017. V. 26 (6). P. 2502-2511.
  26. Lima H.M.L.F., Bastos I.N., Araújo W.S., Martins M. Heat treatment effects on ASTM A890/A 890M GR 5A super duplex stainless steel passivity // Mater Res. 2018. V. 20. Suppl. 2. P. 775-85.
  27. Allou D., Ould Brahim I., Cheniti B., et al. Effect of Post Weld Heat Treatment on Microstructure and Mechanical Behaviors of Weld Overlay Inconel 182 on 4130 Steel Substrate Using SMAW Process Metallography // Microstructure and Analysis. 2021. V. 10 (5). P. 567-578.

Declaração de direitos autorais © Russian Academy of Sciences, 2023

Este site utiliza cookies

Ao continuar usando nosso site, você concorda com o procedimento de cookies que mantêm o site funcionando normalmente.

Informação sobre cookies