Refinement of the phase diagram of the MnSe– Ga2Se3 system

Capa

Citar

Texto integral

Acesso aberto Acesso aberto
Acesso é fechado Acesso está concedido
Acesso é fechado Somente assinantes

Resumo

Phase equilibria in the MnSe–Ga2Se3 system were re-investigated by differential thermal analysis (DTA) and X-ray diffraction (XRD) methods and its phase diagram was constructed, which somewhat differs from that presented earlier in the literature. It was established that the system is characterized by the formation of an intermediate phase (ã) with a wide (47–61 mol % Ga2Se3) homogeneity region. Based on Ga2Se3, a wide (~30 mol %) areas of solid solutions was also found. It is shown that the ã-phase undergoes a polymorphic transformation ã′↔ã at 1183 – 1193 K for various compositions. The high-temperature ã′-phase has a minimum melting at 1205 K and 55 mol% Ga2Se3 and is in peritectic equilibria with solid solutions based on both initial binary compounds. Based on powder diffraction data, the tetragonal lattice parameters of the ã-phase with compositions of 50 and 60 mol % Ga2Se3 were determined. The previously indicated ternary compound of the Mn2Ga2Se5 composition was not been confirmed. A comparative analysis of the obtained results with literature data was carried out.

Texto integral

Acesso é fechado

Sobre autores

F. Mammadov

Institute of Catalysis and Inorganic Chemistry; Azerbaijan State Pedagogical University

Autor responsável pela correspondência
Email: faikmamadov@mail.ru
Azerbaijão, AZ-1143 Baku; AZ-1000, Baku

R. Agayeva

Azerbaijan State Pedagogical University

Email: faikmamadov@mail.ru
Azerbaijão, AZ-1000, Baku

I. Amiraslanov

Institute of Physics

Email: faikmamadov@mail.ru
Azerbaijão, AZ-1143, Baku

M. Babanly

Institute of Catalysis and Inorganic Chemistry

Email: faikmamadov@mail.ru
Azerbaijão, AZ-1143 Baku

Bibliografia

  1. Hyunjung K., Tiwari A.P., Hwang E. et al. // Adv. Sci. 2018. V. 5. № 7. P. 1800068. https://doi.org/10.1002/advs.201800068
  2. Xia C., Li J. // J. Semicond. 2016. V. 37. № 5. P. 051001. https://doi.org/10.1088/1674-4926/37/5/051001
  3. Wyżga P., Veremchuk I., Bobnar M. et al. // Z. Anorg. Allg. Chem. 2020. V. 646. № 14. P. 1091. https://doi.org/10.1002/zaac.202000014
  4. Karthikeyan N., Aravindsamy G., Balamurugan P. et al. // Mater. Res. Innovations. 2018. V. 22. № 5. Р. 278. https://doi.org/10.1080/14328917.2017.1314882
  5. Bose A., Banerjee R., Narayan A. // Condens. Matter. 2022. V. 2. P. 1. https://arxiv.org/pdf/2202.03317v2.pdf
  6. Yang J., Zhou Z., Fang J. et al. // Appl. Phys. Lett. 2019. V. 115. № 22. P. 222101. https://doi.org/10.1063/ 1.5126233
  7. Hwang Y., Choi J., Ha Y. et al. // Curr. Appl. Phys. 2020. V. 20. № 1. P. 212. https://doi.org/10.1016/j.cap.2019. 11.005
  8. Sagredo V., Torres T.E., Delgado G.E. et al. // Rev. Mex. Fís. 2019. V. 65. № 1. P. 14. https://www.scielo.org.mx/scielo.php?script=sci_arttext&pid=S0035-001X2019000100014
  9. Zhang B., Liu Y., Zhu H. et al. // Environ. Sci. Pollut. Res. 2023. V. 30. P. 13438. https://doi.org/10.1007/s11356-022-22929-6
  10. Pauliukavets S.A., Bychek I.V., Patapovich M.P. // Inorg. Mater: Appl. Res. 2018. V. 9. № 2. P. 207. https://doi.org/10.1134/S2075113318020223 [Павлюковец С.А., Бычек И.В., Патапович М.П. // Перспективные материалы. 2017. № 12. С. 26. https://www.j-pm.ru/12-articles-1-9]
  11. Kim H., Liu X., Kim M. et al. // Chem. Mater. 2021. V. 33. № 1. P. 164. https://doi.org/10.1021/acs.chemmater.0c03146
  12. Eremeev S.V., Otrokov M.M., Chulkov E.V. // Nano Lett. 2018. V. 18. № 10. P. 6521. https://doi.org/10.1021/acs.nanolett.8b03057
  13. Otrokov M.M., Klimovskikh I.I., Bentmann H. et al. // Nature. 2019. V. 576. № 7787. P. 416. https://doi.org/10.1038/s41586-019-1840-9
  14. Haoyu L., Yiya H., Qixun G. et al. // J. Phys. D: Appl. Phys. 2023. V. 56. № 4. P. 045302. https://doi.org/ 10.1088/1361-6463/aca61e
  15. Klimovskikh I.I., Otrokov M.M., Estyunin D. et al. // npj Quantum Mater. 2020. V. 5. № 54. https://doi.org/ 10.1038/s41535-020-00255-9
  16. Estyunin D.A., Klimovskikh I.I., Shikin A.M. et al. // APL Mater. 2020. V. 8. № 2. P. 021105. https://doi.org/ 10.1063/1.5142846
  17. Walko R.C., Zhu T., Bishop A.J. et al. // Phys. E. 2022. V. 143. P. 115391. https://doi.org/10.1016/j.physe. 2022.115391
  18. Yonghao Y., Xintong W., Hao L. et al. // Nano Lett. 2020. V. 20. № 5. P. 3271. https://dx.doi.org/10.1021/acs.nanolett.0c00031
  19. Zhou L., Tan Z., Yan D. et al. // Phys. Rev. B: Condens. Matter. 2020. V. 102. № 8. P. 085114. https://doi.org/ 10.1103/PhysRevB.102.085114
  20. Garrity K.F., Chowdhury S., Tavazza F.M. // Phys. Rev. Materials. 2021. V. 5. № 2. P. 024207. https://doi.org/ 10.1103/PhysRevMaterials.5.024207
  21. Ovchinnikov D., Huang X., Lin Z. et al. // Nano Lett. 2021. V. 21. № 6. P. 2544. https://dx.doi.org/10.1021/acs.nanolett.0c05117
  22. Swatek P., Wu Y., Wang L.L. // Phys. Rev. B: Condens. Matter. 2020. V. 101. № 16. P. 161109. https://doi.org/ 10.1103/PhysRevB.101.161109
  23. Zhu T., Bishop A.J., Zhou T. et al. // Nano Lett. 2021. V. 21. № 12. P. 5083. https://doi.org/10.1021/acs.nanolett.1c00141
  24. Garnica M., Otrokov M., Aguilar P.C. et al. // npj Quantum Mater. 2022. V. 7. P. 1. https://doi.org/ 10.1038/s41535-021-00414-6
  25. Sharan A., Sajjad M., Singh D.J. et al. // Phys. Rev. Materials. 2022. V. 6. № 9. P. 094005. https://doi.org/ 10.1103/PhysRevMaterials.6.094005
  26. Tarasov A.V., Makarova T.P., Estyunin D.A. et al. // Symmetry. 2023. V. 15. № 2. P. 469. https://doi.org/10.3390/sym15020469
  27. Djieutedjeu H., Lopez J.S., Lu R. et al. // J. Am. Chem. Soc. 2019. V. 141. № 23. P. 9249. https://doi.org/10.1021/jacs.9b01884
  28. Levy I., Forrester C., Ding X. et al. // Scientific Reports. 2023. V. 13. P. 7381. https://doi.org/10.1038/s41598-023-34585-y
  29. Moroz N.A., Lopez J.S., Djieutedjeu H. et al. // Chem. Mater. 2016. V. 28. № 23. P. 8570. https://doi.org/ 10.1021/acs.chemmater.6b03293
  30. Levy I., Forrester C., Deng H. et al. // Cryst. Growth Des. 2022. V. 22. № 5. P. 3007. https://doi.org/10.1021/acs.cgd.1c01453
  31. Liu Y., Kang Ch., Stavitski E. et al. // Phys. Rev. B. 2018. V. 97. № 15. P. 155202. https://doi.org/10.1103/PhysRevB.97.155202
  32. Babanly M.B., Chulkov E.V., Aliev Z.S. et al. // Russ. J. Inorg. Chem. 2017. V. 62. № 13. P. 1703. https://doi.org/10.1134/S0036023617130034
  33. Babanly M.B., Mashadiyeva L.F., Babanly D.M. et al. // Russ. J. Inorg. Chem. 2019. V. 64. № 13. P. 1649. https://doi.org/10.1134/S0036023619130035
  34. Imamaliyeva S.Z., Babanly D.M., Qasymov V.A. et al. // Russ. J. Inorg. Chem. 2021. V. 66. № 4. Р. 558. https://doi.org/10.1134/S0036023621040124 [Имамалиева С.З., Бабанлы Д.М., Гасымов В.А. и др. // Журн. неорган. химии. 2021. T. 66. № 4. C. 519. https://doi.org/10.31857/S0044457X21040127]
  35. Mammadov F.M., Amiraslanov I.R., Imamaliyeva S.Z. et al. // J. Phase Equilib. Diffus. 2019. V. 40. № 6. P. 787. https://doi.org/10.1007/s11669-019-00768-2
  36. Mamedov F.M., Babanly D.M., Amiraslanov I.R. et al. // Russ. J. Inorg. Chem. 2020. V. 65. № 11. P. 1747. https://doi.org/10.1134/S0036023620110121 [Мамедов Ф.М., Бабанлы Д.М., Амирасланов И.Р. и др. // Журн. неорган. химии. 2020. T. 65. № 11. C. 1535. https://doi.org/10.31857/S0044457X20110124]
  37. Mammadov F.М., Amiraslanov I.R., Aliyeva Y.R. et al. // Acta Chim. Slovenica. 2019. V. 66. P. 466. https://doi.org/10.17344/acsi.2019.4988
  38. Mammadov F.M., Babanly D.M., Amiraslanov I.R. et al. // Russ. J. Inorg. Chem. 2021. V. 66. № 10. P. 1533. https://doi.org/10.1134/S0036023621100090 [Мамедов Ф.М., Бабанлы Д.М., Амирасланов И.Р. и др. // Журн. неорган. химии. 2021. T. 66. № 10. C. 1457. https://doi.org/ 10.31857/S0044457X21100093]
  39. Mammadov F.M., Niftiev N.N., Jafarov Ya.I. et al. // Russ. J. Inorg. Chem. 2022. V. 67. № 10. P. 1623. https://doi.org/10.1134/S0036023622600769 [Мамедов Ф.М., Нифтиев Н.Н., Джафаров Я.И. и др. // Журн. неорган. химии. 2022. T. 67. № 10. C. 1459. https://doi.org/ 10.31857/S0044457X22100142]
  40. Pardo M.P., Flahaut J. // Mater. Res. Bull. 1978. V. 13. № 11. P. 1231. https://doi.org/10.1016/0025-5408(78) 90214-3
  41. Бабаева П.К., Рустамов П.Г. // Исследования в области неорганической и физической химии. Баку: Элм, 1981. C. 53.
  42. Диаграммы состояния двойных металлических систем / Под ред. Лякишева Н.Р. М.: Машиностроение, 2001. Т. 3. Кн. 1. С. 382.
  43. Massalski T.B. Binary alloy phase diagrams. Ohio: ASM İnternational. Materials Park, 1990. 3875 p.
  44. Абрикосов Н.Х., Банкина В.Ф., Порецкая Л.В. и др. Полупроводниковые халькогениды и сплавы на их основе. М.: Наука, 1975. 220 с.
  45. Cannas M., Garbato L., Geddo Lehmann A. et al. // Cryst. Res. Technol. 1998. V. 33. № 3. P. 417. https://doi.org/10.1002/(SICI)1521-4079(1998)33:3<417::AID-CRAT417>3.0.CO;2-2

Arquivos suplementares

Arquivos suplementares
Ação
1. JATS XML
Baixar
2. Fig. 1. Powder diffraction patterns of alloys of the MnSe–Ga2Se3 system.

Baixar (1MB)
Metadados
3. Fig. 2. Phase diagram of the MnSe–Ga2Se3 system.

Baixar (830KB)
Metadados
4. Fig. 3. Powder diffraction pattern of a sample of MnGa2Se4 composition, quenched from 1200 K.

Baixar (694KB)
Metadados
5. Fig. 4. DTA heating curves for some annealed alloys of the MnSe–Ga2Se3 system: 1 - 40, 2 - 50, 3 - 65 mol. % Ga2Se3.

Baixar (846KB)
Metadados

Declaração de direitos autorais © Russian Academy of Sciences, 2024

Este site utiliza cookies

Ao continuar usando nosso site, você concorda com o procedimento de cookies que mantêm o site funcionando normalmente.

Informação sobre cookies