Structure and Electrical Conductivity of Bismuth- and Germanium-Doped Calcium Molybdates

Мұқаба

Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Тек жазылушылар үшін

Аннотация

Ca1 – 2xBi2xMo1 – xGexO4 solid solutions with a scheelite-like structure (space group I41/a) and the homogeneity range х = 0.0–0.4 were prepared using standard ceramic technology. The unit cell parameter с and unit cell volume increase as the dopant concentration increases due to the changing size of Ca/BiO8 polyhedra. The predominant thermal expansion of Ca/BiO8 polyhedra was inferred from the temperature-dependent unit cell parameters and Raman spectral patterns. The Ca/Bi–O and Mo/Ge–O bond lengths were calculated. The increasing dopant concentration decreases the thermal expansion coefficient of the ceramics and increases the electrical conductivity and activation energy of the complex oxides compared to the matrix compound. The effective oxygen diffusion coefficient is determined.

Авторлар туралы

O. Kaimieva

Eltsin Ural Federal University, Institute of Natural Sciences and Mathematics

Email: kaimi-olga@mail.ru
620000, Yekaterinburg, Russia

Z. Mikhailovskaya

Eltsin Ural Federal University, Institute of Natural Sciences and Mathematics; Zavaritskii Institute of Geology and Geochemistry, Ural Branch, Russian Academy of Sciences

Email: kaimi-olga@mail.ru
620000, Yekaterinburg, Russia; 620110, Yekaterinburg, Russia

E. Buyanova

Eltsin Ural Federal University, Institute of Natural Sciences and Mathematics

Email: kaimi-olga@mail.ru
620000, Yekaterinburg, Russia

S. Petrova

Institute of Metallurgy, Ural Branch, Russian Academy of Sciences

Email: kaimi-olga@mail.ru
620016, Yekaterinburg, Russia

E. Pankrushina

Zavaritskii Institute of Geology and Geochemistry, Ural Branch, Russian Academy of Sciences

Хат алмасуға жауапты Автор.
Email: kaimi-olga@mail.ru
620110, Yekaterinburg, Russia

Әдебиет тізімі

  1. Kato H., Matsudo N., Kudo A. // Chem. Lett. 2004. V. 33. № 9. P. 1216. https://doi.org/10.1246/cl.2004.1216
  2. Ramarao S.D., Roopas Kiran S., Murthy V.R.K. // Mater. Res. Bull. 2014. V. 56. P. 71. https://doi.org/10.1016/j.materresbull.2014.04.064
  3. Choi G.-K., Kim J., Yoon S.H. et al. // J. Eur. Ceram. Soc. 2007. V. 27. № 1. P. 3063. https://doi.org/10.1016/j.jeurceramsoc.2006.11.037
  4. Mikhailik V.B., Kraus H., Miller G. et al. // J. Appl. Phys. 2005. V. 97. № 8. P. 083523. https://doi.org/10.1063/1.1872198
  5. Maji B.K., Jena H., Asuvathraman R. et al. // J. Alloys Compd. 2015. V. 640. P. 475. https://doi.org/10.1016/j.jallcom.2015.04.054
  6. Petrov A., Kofstad P. // J. Solid State Chem. 1979. V. 30. P. 83. https://doi.org/10.1016/0022-4596(79)90133-6
  7. Im H.-N., Choi M.-B., Jeon S.-Y. et al. // Ceram. Int. 2011. V. 37. P. 49. https://doi.org/10.1016/j.ceramint.2010.08.004
  8. Cheng J., Liu Ch., Cao W. et al. // Mater. Res. Bull. 2011. V. 46. P. 185. https://doi.org/10.1016/j.materresbull.2010.11.019
  9. Arora S.K., Godbole R.S., Lakshminarayana D. // J. Mater. Sci. 1983. V. 18. P. 1359. https://doi.org/10.1007/BF01111955
  10. Cheng J., Bao W., Han Ch. et al. // J. Power Sources. 2010. V. 195. P. 1849. https://doi.org/10.1016/j.jpowsour.2009.10.017
  11. Cheng J., He J. // Mater. Lett. 2017. V. 209. P. 525. https://doi.org/10.1016/j.matlet.2017.08.094
  12. Esaka T. // Solid State Ionics. 2000. V. 136–137. P. 1. https://doi.org/10.1016/S0167-2738(00)00377-5
  13. Bollmann W. // Cryst. Res. Technol. 1978. V. 18. № 8. P. 100. https://doi.org/10.1002/crat.19780130816
  14. Rigdon M.A., Grace R.E. // J. Am. Ceram. Soc. 1973. V. 56. № 9. P. 475. https://doi.org/10.1111/j.1151-2916.1973.tb12527.x
  15. Guo H.-H., Zhou D., Pang L.-X. et al. // J. Eur. Ceram. Soc. 2019. V. 39. P. 2365. https://doi.org/10.1016/j.jeurceramsoc.2019.02.010
  16. Mikhaylovskaya Z.A., Buyanova E.S., Petrova S.A. et al. // Chim. Techno Acta. 2021. V. 8. № 2. P. 20218204. https://doi.org/10.15826/chimtech.2021.8.2.04
  17. Мацкевич Н.И., Семерикова А.Н., Гельфонд Н.В. и др. // Журн. неорган. химии. 2020. Т. 65. № 5. С. 669. https://doi.org/10.31857/S0044457X20050165
  18. Дергачева П.Е., Кульбакин И.В., Ашмарин А.А. и др. // Журн. неорган. химии. 2021. Т. 66. № 8. С. 1126. https://doi.org/10.31857/S0044457X21080043
  19. Каймиева О.С., Сабирова И.Э., Буянова Е.С. и др. // Журн. неорган. химии. 2022. Т. 67. № 9. С. 1211. https://doi.org/10.31857/S0044457X22090057
  20. Емельянова Ю.В., Морозова М.В., Михайловская З.А. и др. // Электрохимия. 2009. Т. 45. № 4. С. 407.
  21. Laugier J., Bochu B. LMGP-Suite of Programs for the interpretation of X-ray Experiments/ENSP. Grenoble: Lab. Materiaux Genie Phys, 2003.
  22. Бубнова Р.С., Фирсова В.А., Филатов С.К. // Физика и химия стекла. 2013. Т. 39. № 3. С. 505.
  23. Peercy P.S., Samara G.A. // Phys. Rev. B. 1973. V. 8. № 5. P. 2033. https://doi.org/10.1103/PHYSREVB.8.2033
  24. Климова А.В., Михайловская З.А., Буянова Е.С. и др. // Электрохимия. 2021. Т. 57. № 8. С. 457. https://doi.org/10.31857/S0424857021080053
  25. Achary S.N., Patwe S.J., Mathews M.D. et al. // J. Phys. Chem. Solids. 2006. V. 67. P. 774. https://doi.org/10.1016/j.jpcs.2005.11.009
  26. Shannon R.D. // Acta Crystallogr., Sect. A: Found. Crystallogr. 1976. V. 32. P. 751. https://doi.org/10.1107/S0567739476001551
  27. Zverev P.G. // Phys. Stat Solid C. 2004. V. 1. № 11. P. 3101. https://doi.org/10.1002/PSSC.200405413
  28. Mikhaylovskaya Z.A., Buyanova E.S., Petrova S.A. et al. // Chim. Techno Acta. 2022. V. 9. № 4. P. 20229410. https://doi.org/10.15826/chimtech.2022.9.4.10
  29. Rietveld H.M. // J. Appl. Crystalogr. 1969. V. 2. P. 65. https://doi.org/10.1107/S0021889869006558
  30. Mikhaylovskaya Z.A., Abrahams I., Petrova S.A. et al. // J. Solid State Chem. 2020. V. 291. P. 121627. https://doi.org/10.1016/j.jssc.2020.121627
  31. Irvine J.T.S., Sinclair D.C., West A.R. // Adv. Mater. 1990. V. 2. № 3. P. 132. https://doi.org/10.1002/adma.19900020304
  32. Abraham Y.B., Holzwarth N.A.W., Williams R.T. et al. // Phys. Rev. B. 2001. V. 64. № 24. P. 245109. https://doi.org/10.1103/PhysRevB.64.245109
  33. Zhao H., Zhang F., Guo X. et al. // J. Phys. Chem. Solids. 2010. V. 71. P. 1639. https://doi.org/10.1016/j.jpcs.2010.08.013

© О.С. Каймиева, З.А. Михайловская, Е.С. Буянова, С.А. Петрова, Е.А. Панкрушина, 2023

Согласие на обработку персональных данных с помощью сервиса «Яндекс.Метрика»

1. Я (далее – «Пользователь» или «Субъект персональных данных»), осуществляя использование сайта https://journals.rcsi.science/ (далее – «Сайт»), подтверждая свою полную дееспособность даю согласие на обработку персональных данных с использованием средств автоматизации Оператору - федеральному государственному бюджетному учреждению «Российский центр научной информации» (РЦНИ), далее – «Оператор», расположенному по адресу: 119991, г. Москва, Ленинский просп., д.32А, со следующими условиями.

2. Категории обрабатываемых данных: файлы «cookies» (куки-файлы). Файлы «cookie» – это небольшой текстовый файл, который веб-сервер может хранить в браузере Пользователя. Данные файлы веб-сервер загружает на устройство Пользователя при посещении им Сайта. При каждом следующем посещении Пользователем Сайта «cookie» файлы отправляются на Сайт Оператора. Данные файлы позволяют Сайту распознавать устройство Пользователя. Содержимое такого файла может как относиться, так и не относиться к персональным данным, в зависимости от того, содержит ли такой файл персональные данные или содержит обезличенные технические данные.

3. Цель обработки персональных данных: анализ пользовательской активности с помощью сервиса «Яндекс.Метрика».

4. Категории субъектов персональных данных: все Пользователи Сайта, которые дали согласие на обработку файлов «cookie».

5. Способы обработки: сбор, запись, систематизация, накопление, хранение, уточнение (обновление, изменение), извлечение, использование, передача (доступ, предоставление), блокирование, удаление, уничтожение персональных данных.

6. Срок обработки и хранения: до получения от Субъекта персональных данных требования о прекращении обработки/отзыва согласия.

7. Способ отзыва: заявление об отзыве в письменном виде путём его направления на адрес электронной почты Оператора: info@rcsi.science или путем письменного обращения по юридическому адресу: 119991, г. Москва, Ленинский просп., д.32А

8. Субъект персональных данных вправе запретить своему оборудованию прием этих данных или ограничить прием этих данных. При отказе от получения таких данных или при ограничении приема данных некоторые функции Сайта могут работать некорректно. Субъект персональных данных обязуется сам настроить свое оборудование таким способом, чтобы оно обеспечивало адекватный его желаниям режим работы и уровень защиты данных файлов «cookie», Оператор не предоставляет технологических и правовых консультаций на темы подобного характера.

9. Порядок уничтожения персональных данных при достижении цели их обработки или при наступлении иных законных оснований определяется Оператором в соответствии с законодательством Российской Федерации.

10. Я согласен/согласна квалифицировать в качестве своей простой электронной подписи под настоящим Согласием и под Политикой обработки персональных данных выполнение мною следующего действия на сайте: https://journals.rcsi.science/ нажатие мною на интерфейсе с текстом: «Сайт использует сервис «Яндекс.Метрика» (который использует файлы «cookie») на элемент с текстом «Принять и продолжить».