Modifiing Effect of Zirconia Nanoparticles during Electric Arc Welding
- 作者: Fominykh M.1, Denisova E.1, Berezovskii A.1, Finkel’shtein A.1, Kartashev V.1
-
隶属关系:
- Ural Federal University,
- 期: 卷 2018, 编号 8 (2018)
- 页面: 783-786
- 栏目: Article
- URL: https://journals.rcsi.science/0036-0295/article/view/172088
- DOI: https://doi.org/10.1134/S0036029518080050
- ID: 172088
如何引用文章
详细
The structure of the weld metal after welding using a flux-cored wire with the addition of 0.3% zirconia flaky nanoparticles is studied. The weld consists of an acicular ferrite. This finding can indicate that the dissociation of zirconia in an electric arc is not an obstacle to a modifying effect, which manifests itself in both the interaction of zirconium with oxygen and the surface activity of zirconium in an iron-based solidifying melt. Thus, zirconia is a modifier of both the first and second kinds for the solidifying weld metal. Excess oxygen is likely to form individual pores less than 1 μm in diameter in the weld metal; however, they only wealy affect the mechanical properties of the welded joint. These results will be used to develop electrode materials for welding pipe steels.
作者简介
M. Fominykh
Ural Federal University,
Email: avinkel@mail.ru
俄罗斯联邦, Yekaterinburg, 620002
E. Denisova
Ural Federal University,
Email: avinkel@mail.ru
俄罗斯联邦, Yekaterinburg, 620002
A. Berezovskii
Ural Federal University,
Email: avinkel@mail.ru
俄罗斯联邦, Yekaterinburg, 620002
A. Finkel’shtein
Ural Federal University,
编辑信件的主要联系方式.
Email: avinkel@mail.ru
俄罗斯联邦, Yekaterinburg, 620002
V. Kartashev
Ural Federal University,
Email: avinkel@mail.ru
俄罗斯联邦, Yekaterinburg, 620002
![](/img/style/loading.gif)