- Авторы: Fominykh M.1, Denisova E.1, Berezovskii A.1, Finkel’shtein A.1, Kartashev V.1
-
Учреждения:
- Ural Federal University,
- Выпуск: Том 2018, № 8 (2018)
- Страницы: 783-786
- Раздел: Article
- URL: https://journals.rcsi.science/0036-0295/article/view/172088
- DOI: https://doi.org/10.1134/S0036029518080050
- ID: 172088
Цитировать
Аннотация
The structure of the weld metal after welding using a flux-cored wire with the addition of 0.3% zirconia flaky nanoparticles is studied. The weld consists of an acicular ferrite. This finding can indicate that the dissociation of zirconia in an electric arc is not an obstacle to a modifying effect, which manifests itself in both the interaction of zirconium with oxygen and the surface activity of zirconium in an iron-based solidifying melt. Thus, zirconia is a modifier of both the first and second kinds for the solidifying weld metal. Excess oxygen is likely to form individual pores less than 1 μm in diameter in the weld metal; however, they only wealy affect the mechanical properties of the welded joint. These results will be used to develop electrode materials for welding pipe steels.
Ключевые слова
Об авторах
M. Fominykh
Ural Federal University,
Email: avinkel@mail.ru
Россия, Yekaterinburg, 620002
E. Denisova
Ural Federal University,
Email: avinkel@mail.ru
Россия, Yekaterinburg, 620002
A. Berezovskii
Ural Federal University,
Email: avinkel@mail.ru
Россия, Yekaterinburg, 620002
A. Finkel’shtein
Ural Federal University,
Автор, ответственный за переписку.
Email: avinkel@mail.ru
Россия, Yekaterinburg, 620002
V. Kartashev
Ural Federal University,
Email: avinkel@mail.ru
Россия, Yekaterinburg, 620002