Estimation of the notch sensitivity of a nitrided steel by acoustic emission

Resumo

The notch sensitivity of sheet corrosion-resistant 08Kh17T steel is estimated in the states before and after high-temperature (1000–1100°C) internal nitriding during tensile tests accompanied by the measurement of acoustic emission signals. A crack in the steel is shown to propagate according to a ductile mechanism is all states. As the nitrogen content increases from 0.60 to 0.85%, the ultimate tensile strength of the steel decreases by 15% in the presence of a stress concentrator and remains substantially higher than the yield strength of the sheet steel without a stress concentrator.