Thermal analysis for modeling the aluminothermic reduction of zirconium from oxide
- Autores: Vedmid’ L.1,2, Agafonov S.1, Avraamov Y.2, Il’inykh M.2, Merkushev A.2, Plotnikov M.2, Terlyga A.2
-
Afiliações:
- Institute of Metallurgy, Ural Branch
- Ural Federal University
- Edição: Volume 2017, Nº 8 (2017)
- Páginas: 652-654
- Seção: Article
- URL: https://journals.rcsi.science/0036-0295/article/view/171642
- DOI: https://doi.org/10.1134/S0036029517080122
- ID: 171642
Citar
Resumo
The modeling of zirconium reduction from oxide by thermal analysis shows that the congruently stable intermetallic compound Al3Zr is formed as a result of the process. The formation of Al3Zr proceeds via the stage of formation of intermediate zirconium monoxide.
Palavras-chave
Sobre autores
L. Vedmid’
Institute of Metallurgy, Ural Branch; Ural Federal University
Autor responsável pela correspondência
Email: elarisa@mail.ru
Rússia, ul. Amundsena 101, Yekaterinburg, 620016; ul. Mira 19, Yekaterinburg, 620002
S. Agafonov
Institute of Metallurgy, Ural Branch
Email: elarisa@mail.ru
Rússia, ul. Amundsena 101, Yekaterinburg, 620016
Yu. Avraamov
Ural Federal University
Email: elarisa@mail.ru
Rússia, ul. Mira 19, Yekaterinburg, 620002
M. Il’inykh
Ural Federal University
Email: elarisa@mail.ru
Rússia, ul. Mira 19, Yekaterinburg, 620002
A. Merkushev
Ural Federal University
Email: elarisa@mail.ru
Rússia, ul. Mira 19, Yekaterinburg, 620002
M. Plotnikov
Ural Federal University
Email: elarisa@mail.ru
Rússia, ul. Mira 19, Yekaterinburg, 620002
A. Terlyga
Ural Federal University
Email: elarisa@mail.ru
Rússia, ul. Mira 19, Yekaterinburg, 620002
![](/img/style/loading.gif)