Thermal analysis for modeling the aluminothermic reduction of zirconium from oxide
- Авторы: Vedmid’ L.1,2, Agafonov S.1, Avraamov Y.2, Il’inykh M.2, Merkushev A.2, Plotnikov M.2, Terlyga A.2
-
Учреждения:
- Institute of Metallurgy, Ural Branch
- Ural Federal University
- Выпуск: Том 2017, № 8 (2017)
- Страницы: 652-654
- Раздел: Article
- URL: https://journals.rcsi.science/0036-0295/article/view/171642
- DOI: https://doi.org/10.1134/S0036029517080122
- ID: 171642
Цитировать
Аннотация
The modeling of zirconium reduction from oxide by thermal analysis shows that the congruently stable intermetallic compound Al3Zr is formed as a result of the process. The formation of Al3Zr proceeds via the stage of formation of intermediate zirconium monoxide.
Ключевые слова
Об авторах
L. Vedmid’
Institute of Metallurgy, Ural Branch; Ural Federal University
Автор, ответственный за переписку.
Email: elarisa@mail.ru
Россия, ul. Amundsena 101, Yekaterinburg, 620016; ul. Mira 19, Yekaterinburg, 620002
S. Agafonov
Institute of Metallurgy, Ural Branch
Email: elarisa@mail.ru
Россия, ul. Amundsena 101, Yekaterinburg, 620016
Yu. Avraamov
Ural Federal University
Email: elarisa@mail.ru
Россия, ul. Mira 19, Yekaterinburg, 620002
M. Il’inykh
Ural Federal University
Email: elarisa@mail.ru
Россия, ul. Mira 19, Yekaterinburg, 620002
A. Merkushev
Ural Federal University
Email: elarisa@mail.ru
Россия, ul. Mira 19, Yekaterinburg, 620002
M. Plotnikov
Ural Federal University
Email: elarisa@mail.ru
Россия, ul. Mira 19, Yekaterinburg, 620002
A. Terlyga
Ural Federal University
Email: elarisa@mail.ru
Россия, ul. Mira 19, Yekaterinburg, 620002