Wear resistance of the oxide layers formed on AK9pch silumin by microarc oxidation in an electrolyte modified by silicon dioxide nanoparticles
- Autores: Polunin A.1, Ivashin P.1, Rastegaev I.1, Borgardt E.1, Krishtal M.1
-
Afiliações:
- Tolyatti State University
- Edição: Volume 2016, Nº 4 (2016)
- Páginas: 385-388
- Seção: Applied Problems of Strength and Plasticity
- URL: https://journals.rcsi.science/0036-0295/article/view/170499
- DOI: https://doi.org/10.1134/S0036029516040194
- ID: 170499
Citar
Resumo
The structure, the phase composition, the surface morphology, the microhardness, and the tribological characteristics of the oxide layers of various thicknesses formed on AK9pch alloy during microarc oxidation are studied. A positive influence of a small addition (5 g/L) of nanosized silicon dioxide to an electrolyte on these characteristics of the oxide layers is revealed.
Sobre autores
A. Polunin
Tolyatti State University
Autor responsável pela correspondência
Email: anpo186@gmail.com
Rússia, ul. Belorusskaya 14, Togliatti, 445667
P. Ivashin
Tolyatti State University
Email: anpo186@gmail.com
Rússia, ul. Belorusskaya 14, Togliatti, 445667
I. Rastegaev
Tolyatti State University
Email: anpo186@gmail.com
Rússia, ul. Belorusskaya 14, Togliatti, 445667
E. Borgardt
Tolyatti State University
Email: anpo186@gmail.com
Rússia, ul. Belorusskaya 14, Togliatti, 445667
M. Krishtal
Tolyatti State University
Email: anpo186@gmail.com
Rússia, ul. Belorusskaya 14, Togliatti, 445667