Wear resistance of the oxide layers formed on AK9pch silumin by microarc oxidation in an electrolyte modified by silicon dioxide nanoparticles
- Авторлар: Polunin A.1, Ivashin P.1, Rastegaev I.1, Borgardt E.1, Krishtal M.1
-
Мекемелер:
- Tolyatti State University
- Шығарылым: Том 2016, № 4 (2016)
- Беттер: 385-388
- Бөлім: Applied Problems of Strength and Plasticity
- URL: https://journals.rcsi.science/0036-0295/article/view/170499
- DOI: https://doi.org/10.1134/S0036029516040194
- ID: 170499
Дәйексөз келтіру
Аннотация
The structure, the phase composition, the surface morphology, the microhardness, and the tribological characteristics of the oxide layers of various thicknesses formed on AK9pch alloy during microarc oxidation are studied. A positive influence of a small addition (5 g/L) of nanosized silicon dioxide to an electrolyte on these characteristics of the oxide layers is revealed.
Авторлар туралы
A. Polunin
Tolyatti State University
Хат алмасуға жауапты Автор.
Email: anpo186@gmail.com
Ресей, ul. Belorusskaya 14, Togliatti, 445667
P. Ivashin
Tolyatti State University
Email: anpo186@gmail.com
Ресей, ul. Belorusskaya 14, Togliatti, 445667
I. Rastegaev
Tolyatti State University
Email: anpo186@gmail.com
Ресей, ul. Belorusskaya 14, Togliatti, 445667
E. Borgardt
Tolyatti State University
Email: anpo186@gmail.com
Ресей, ul. Belorusskaya 14, Togliatti, 445667
M. Krishtal
Tolyatti State University
Email: anpo186@gmail.com
Ресей, ul. Belorusskaya 14, Togliatti, 445667
![](/img/style/loading.gif)