Corrosion of Various Types of Stainless Steel in Chloroaluminate Melts
- Авторлар: Karpov V.1, Abramov A.1, Dedov K.1, Shak A.1, Zhilyakov A.1, Polovov I.1, Belikov S.1, Rebrin O.1
-
Мекемелер:
- Ural Federal University
- Шығарылым: Том 2019, № 2 (2019)
- Беттер: 190-193
- Бөлім: Article
- URL: https://journals.rcsi.science/0036-0295/article/view/173069
- DOI: https://doi.org/10.1134/S0036029519020101
- ID: 173069
Дәйексөз келтіру
Аннотация
The corrosion behavior of austenitic steels AISI 316L (analog of 03Kh16N15M3), 12Kh18N10T (analog of AISI 321) and 06KhN28MDT and ferritic and ferritic–martensitic steels 12Kh13 (analog of AISI 410), 08Kh17T (analog of AISI 439), and 16Kh12MVSFBR is studied in chloroaluminate melts at a temperature of 550°C. The corrosion rates of these steels in a KCl–AlCl3 electrolyte are determined. The corrosion damage of the stainless steel surfaces is shown to have a continuous inhomogeneous character and to be characterized by etching off the most electronegative elements, namely, chromium, iron, and manganese.
Негізгі сөздер
Авторлар туралы
V. Karpov
Ural Federal University
Хат алмасуға жауапты Автор.
Email: karpov610@yandex.ru
Ресей, Yekaterinburg, 620002
A. Abramov
Ural Federal University
Email: karpov610@yandex.ru
Ресей, Yekaterinburg, 620002
K. Dedov
Ural Federal University
Email: karpov610@yandex.ru
Ресей, Yekaterinburg, 620002
A. Shak
Ural Federal University
Email: karpov610@yandex.ru
Ресей, Yekaterinburg, 620002
A. Zhilyakov
Ural Federal University
Email: karpov610@yandex.ru
Ресей, Yekaterinburg, 620002
I. Polovov
Ural Federal University
Email: karpov610@yandex.ru
Ресей, Yekaterinburg, 620002
S. Belikov
Ural Federal University
Email: karpov610@yandex.ru
Ресей, Yekaterinburg, 620002
O. Rebrin
Ural Federal University
Email: karpov610@yandex.ru
Ресей, Yekaterinburg, 620002
![](/img/style/loading.gif)