Thermal Conductivity of Low-Alloy Copper for Molds
- Авторлар: Dubskii G.1, Vdovin K.1, Nefed’ev A.1, Egorova L.1
-
Мекемелер:
- Magnitogorsk State Technical University
- Шығарылым: Том 2018, № 3 (2018)
- Беттер: 252-258
- Бөлім: Article
- URL: https://journals.rcsi.science/0036-0295/article/view/172417
- DOI: https://doi.org/10.1134/S0036029518030035
- ID: 172417
Дәйексөз келтіру
Аннотация
A setup is created to determine the main thermotechnical characteristics of copper alloys. At temperatures below 400°C, Cu–Fe alloys are found to have the thermal conductivity and the thermal diffusivity that are lower than those of pure copper by a factor of 1.5–2.0. As the temperature increases, these parameters become close to those of pure copper. The wall of a mold made of a copper alloy with 0.17–0.23 wt % iron has a satisfactory thermal conductivity upon heating to 250–300°C.
Негізгі сөздер
Авторлар туралы
G. Dubskii
Magnitogorsk State Technical University
Email: kn.vdovin@gmail.com
Ресей, Magnitogorsk
K. Vdovin
Magnitogorsk State Technical University
Хат алмасуға жауапты Автор.
Email: kn.vdovin@gmail.com
Ресей, Magnitogorsk
A. Nefed’ev
Magnitogorsk State Technical University
Email: kn.vdovin@gmail.com
Ресей, Magnitogorsk
L. Egorova
Magnitogorsk State Technical University
Email: kn.vdovin@gmail.com
Ресей, Magnitogorsk