Choice of quenching temperature and its effect on the structure and properties of a high-strength grade 01979 aluminum alloy
- Authors: Kuptsov S.G.1, Elantsev A.V.1, Nikonenko E.A.1, Nikitina E.V.1,2
-
Affiliations:
- El’tsin Ural Federal University
- Institute of High-Temperature Electrochemistry, Ural Branch
- Issue: Vol 2016, No 8 (2016)
- Pages: 763-770
- Section: Article
- URL: https://journals.rcsi.science/0036-0295/article/view/170799
- DOI: https://doi.org/10.1134/S0036029516080085
- ID: 170799
Cite item
Abstract
Differential scanning calorimetry data are presented for the 01979 alloy produced by granular technology. The optimum quenching temperature is confirmed. Strengthening phases dissolve most completely at this temperature. The phase composition of the high-strength aluminum alloy is studied using scanning microscopy and electron microprobe analysis. The AlCu4, AlCr2, and MgZn2 phases and their interplanar spacings are determined.
About the authors
S. G. Kuptsov
El’tsin Ural Federal University
Email: neekeetina@mail.ru
Russian Federation, ul. Mira 19, Yekaterinburg, 620002
A. V. Elantsev
El’tsin Ural Federal University
Email: neekeetina@mail.ru
Russian Federation, ul. Mira 19, Yekaterinburg, 620002
E. A. Nikonenko
El’tsin Ural Federal University
Email: neekeetina@mail.ru
Russian Federation, ul. Mira 19, Yekaterinburg, 620002
E. V. Nikitina
El’tsin Ural Federal University; Institute of High-Temperature Electrochemistry, Ural Branch
Author for correspondence.
Email: neekeetina@mail.ru
Russian Federation, ul. Mira 19, Yekaterinburg, 620002; ul. S. Kovalevskoi 22, Yekaterinburg, 620219