Мақаланы E-mail арқылы жіберу Choice of quenching temperature and its effect on the structure and properties of a high-strength grade 01979 aluminum alloy
- Авторлар: Kuptsov S.1, Elantsev A.1, Nikonenko E.1, Nikitina E.1,2
-
Мекемелер:
- El’tsin Ural Federal University
- Institute of High-Temperature Electrochemistry, Ural Branch
- Шығарылым: Том 2016, № 8 (2016)
- Беттер: 763-770
- Бөлім: Article
- URL: https://journals.rcsi.science/0036-0295/article/view/170799
- DOI: https://doi.org/10.1134/S0036029516080085
- ID: 170799
Дәйексөз келтіру
Ашық рұқсат
Рұқсат берілді
Тек жазылушылар үшін
Аннотация
Differential scanning calorimetry data are presented for the 01979 alloy produced by granular technology. The optimum quenching temperature is confirmed. Strengthening phases dissolve most completely at this temperature. The phase composition of the high-strength aluminum alloy is studied using scanning microscopy and electron microprobe analysis. The AlCu4, AlCr2, and MgZn2 phases and their interplanar spacings are determined.
Авторлар туралы
S. Kuptsov
El’tsin Ural Federal University
Email: neekeetina@mail.ru
Ресей, ul. Mira 19, Yekaterinburg, 620002
A. Elantsev
El’tsin Ural Federal University
Email: neekeetina@mail.ru
Ресей, ul. Mira 19, Yekaterinburg, 620002
E. Nikonenko
El’tsin Ural Federal University
Email: neekeetina@mail.ru
Ресей, ul. Mira 19, Yekaterinburg, 620002
E. Nikitina
El’tsin Ural Federal University; Institute of High-Temperature Electrochemistry, Ural Branch
Хат алмасуға жауапты Автор.
Email: neekeetina@mail.ru
Ресей, ul. Mira 19, Yekaterinburg, 620002; ul. S. Kovalevskoi 22, Yekaterinburg, 620219