Solid-state oxidation kinetics of an yttrium-containing AK1M2 alloy
- Authors: Berdiev A.E.1, Ganiev I.N.2, Niezov K.K.3
-
Affiliations:
- Russian-Tajik (Slavic) University
- Nikitin Institute of Chemistry
- Osimi Tajik Technical University
- Issue: Vol 2017, No 3 (2017)
- Pages: 200-203
- Section: Article
- URL: https://journals.rcsi.science/0036-0295/article/view/171341
- DOI: https://doi.org/10.1134/S0036029517030028
- ID: 171341
Cite item
Abstract
The interaction of an yttrium-modified AK1M2 alloy with atmospheric oxygen in the temperature range 723–823 K is studied by thermogravimetry. The kinetic parameters of oxidation are determined. An yttrium addition is shown to decrease the oxidation rate, which is accompanied by an increase in the apparent oxidation activation energy from 114.9 to 134.6 kJ/mol.
About the authors
A. E. Berdiev
Russian-Tajik (Slavic) University
Author for correspondence.
Email: berdiev75@mail.ru
Tajikistan, Dushanbe
I. N. Ganiev
Nikitin Institute of Chemistry
Email: berdiev75@mail.ru
Tajikistan, Dushanbe
Kh. Kh. Niezov
Osimi Tajik Technical University
Email: berdiev75@mail.ru
Tajikistan, Dushanbe
![](/img/style/loading.gif)