Solid-state oxidation kinetics of an yttrium-containing AK1M2 alloy
- Авторы: Berdiev A.1, Ganiev I.2, Niezov K.3
-
Учреждения:
- Russian-Tajik (Slavic) University
- Nikitin Institute of Chemistry
- Osimi Tajik Technical University
- Выпуск: Том 2017, № 3 (2017)
- Страницы: 200-203
- Раздел: Article
- URL: https://journals.rcsi.science/0036-0295/article/view/171341
- DOI: https://doi.org/10.1134/S0036029517030028
- ID: 171341
Цитировать
Аннотация
The interaction of an yttrium-modified AK1M2 alloy with atmospheric oxygen in the temperature range 723–823 K is studied by thermogravimetry. The kinetic parameters of oxidation are determined. An yttrium addition is shown to decrease the oxidation rate, which is accompanied by an increase in the apparent oxidation activation energy from 114.9 to 134.6 kJ/mol.
Ключевые слова
Об авторах
A. Berdiev
Russian-Tajik (Slavic) University
Автор, ответственный за переписку.
Email: berdiev75@mail.ru
Таджикистан, Dushanbe
I. Ganiev
Nikitin Institute of Chemistry
Email: berdiev75@mail.ru
Таджикистан, Dushanbe
Kh. Niezov
Osimi Tajik Technical University
Email: berdiev75@mail.ru
Таджикистан, Dushanbe
![](/img/style/loading.gif)