Evolution of the structure and mechanical properties of a bulk-nitrided corrosion-resistant ferritic steel upon tempering in the temperature range of 400–700°C

Аннотация

Methods of the X-ray diffraction analysis and electron microscopy were used to study changes in the structural phase state and mechanical properties of bulk-nitrided 08Kh17T steel (0.08 wt % C, 17 wt % Cr, 0.8 wt % Ti, 0.5 wt % Si, 0.8 wt % Mn, 0.025 wt % S, and 0.035 wt % P) upon tempering in the temperature range of 400–700°C. The changes in the mechanical properties of the nitrided steel upon tempering are associated with the predominance of either the solid-solution or precipitation strengthening, i.e., with the presence of martensite in the steel structure at low temperatures of tempering and the precipitation of particles of Cr₂N nitrides of different dispersity upon increasing the tempering temperature. The greatest increase in the ultimate tensile strength and yield stress (1.8–2.5 times) at a satisfactory plasticity (no less than 10%) of the bulk-nitrided steel is achieved by tempering bulk-nitrided steel in a temperature range of 600–700°C.