A comparative study of microstructure, oxidation resistance, mechanical, and tribological properties of coatings in Mo–B–(N), Cr–B–(N) and Ti–B–(N) systems


Citar

Texto integral

Acesso aberto Acesso aberto
Acesso é fechado Acesso está concedido
Acesso é fechado Somente assinantes

Resumo

M–B–(N) (M = Mo, Cr, Ti) coatings were obtained by the magnetron sputtering of MoB, CrB2, TiB, and TiB2 targets in argon and in gaseous mixtures of argon with nitrogen. The structure and composition of the coatings have been investigated using scanning electron microscopy, glow-discharge optical emission spectroscopy, and X-ray diffraction. The mechanical and tribological properties of the coatings have been determined by nanoindentation, scratch-testing, and ball-on-disk tribological tests. The experiments on estimating the oxidation resistance of coatings were carried out in a temperature range of 600–1000°С. A distinctive feature of TiB2 coatings was their high hardness (61 GPa). The Cr–B–(N) coatings had high maximum oxidation resistance (900°С (CrB2) and 1000°С (Cr–B–N)) and possessed high resistance to the diffusion of elements from the metallic substrate up to a temperature of 1000°С. The Mo–B–N coatings were significantly inferior to the Ti–B–(N) and Cr–B–(N) coatings in their mechanical properties and oxidation resistance, as well as had а tendency to oxidize in air atmosphere after long exposure at room temperature. All of the coatings with nitrogen possessed a low coefficient of friction (in a range of 0.3–0.5) and low relative wear ((0.8–1.2) × 10–6 mm3 N–1 m–1.

Sobre autores

F. Kiryukhantsev-Korneev

National University of Science and Technology MISIS

Autor responsável pela correspondência
Email: kiruhancev-korneev@yandex.ru
Rússia, Moscow, 119049

A. Novikov

National University of Science and Technology MISIS

Email: kiruhancev-korneev@yandex.ru
Rússia, Moscow, 119049

T. Sagalova

National University of Science and Technology MISIS

Email: kiruhancev-korneev@yandex.ru
Rússia, Moscow, 119049

M. Petrzhik

National University of Science and Technology MISIS

Email: kiruhancev-korneev@yandex.ru
Rússia, Moscow, 119049

E. Levashov

National University of Science and Technology MISIS

Email: kiruhancev-korneev@yandex.ru
Rússia, Moscow, 119049

D. Shtansky

National University of Science and Technology MISIS

Email: kiruhancev-korneev@yandex.ru
Rússia, Moscow, 119049

Arquivos suplementares

Arquivos suplementares
Ação
1. JATS XML

Declaração de direitos autorais © Pleiades Publishing, Ltd., 2017