Isothermal Decomposition of β-Solid Solution in Titanium Alloy Ti – 10 V – 2Fe – 3Al


Citar

Texto integral

Acesso aberto Acesso aberto
Acesso é fechado Acesso está concedido
Acesso é fechado Somente assinantes

Resumo

Regular features of variation of structure, phase composition and hardness characteristics in a β-phase-based titanium alloy Ti – 10 V – 2Fe – 3Al subjected to isothermal treatment in a melt of lead and tin for 5 sec – 32 h at 250 – 800 °C after a hold at 860 °C are considered. The types of the phases precipitated in the process of isothermal decomposition of the high-temperature β-solid solution and the dependences of the lattice constant of the β-phase and of the hardness on the temperature-and-time mode of the treatment are determined. Adiagram of isothermal decomposition of the β-solid solution in alloy Ti – 10 V – 2Fe – 3Al is plotted.

Sobre autores

A. Illarionov

Ural Federal University after the First President of Russia B. N. Eltsyn

Autor responsável pela correspondência
Email: illarionovag@mail.ru
Rússia, Ekaterinburg

A. Trubochkin

VSMPO-AVISMA Corporation

Email: illarionovag@mail.ru
Rússia, Verkhnyaya Salda

A. Shalaev

VSMPO-AVISMA Corporation

Email: illarionovag@mail.ru
Rússia, Verkhnyaya Salda

S. Illarionova

Ural Federal University after the First President of Russia B. N. Eltsyn

Email: illarionovag@mail.ru
Rússia, Ekaterinburg

A. Popov

Ural Federal University after the First President of Russia B. N. Eltsyn

Email: illarionovag@mail.ru
Rússia, Ekaterinburg

Arquivos suplementares

Arquivos suplementares
Ação
1. JATS XML

Declaração de direitos autorais © Springer Science+Business Media New York, 2017