Prevention of Crack Formation in Electron-Beam Welded Joints of Dissimilar Metal Compounds (TiNi/Ti6Al4V)


如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

The microstructure, mechanical properties and element distribution in an electron-beam welded joint of dissimilar metal compounds (TiNi/Ti6Al4V) have been studied. To prevent crack formation, niobium was introduced to the compound as a filler material. The welding line preheating and electron-beam deviation toward the Ti6Al4V alloy were used. It was shown that fracturing of the welded joint occurs within the fusion zone and is characterized by a mixed ductile-brittle behavior.

作者简介

Zilin Zhan

National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology of Nanchang

编辑信件的主要联系方式.
Email: 15079293793@163.com
中国, Nanchang

Yuhua Chen

National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology of Nanchang

Email: 15079293793@163.com
中国, Nanchang

Shanlin Wang

National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology of Nanchang

Email: 15079293793@163.com
中国, Nanchang

Yongde Huang

National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology of Nanchang

Email: 15079293793@163.com
中国, Nanchang

Yuqing Mao

National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology of Nanchang

Email: 15079293793@163.com
中国, Nanchang

补充文件

附件文件
动作
1. JATS XML

版权所有 © Springer Science+Business Media, LLC, part of Springer Nature, 2019