Effect of Crystal Structure Fineness for Charge Alloy AK6M2 on Its Flux Treatment Efficiency
- Authors: Nikitin K.V.1, Nikitin V.I.1, Timoshkin I.Y.1, Chikova O.A.2
-
Affiliations:
- Samara State Technical University
- Ural Federal University named after the first President of Russia B. N. El’tsin
- Issue: Vol 58, No 5-6 (2016)
- Pages: 279-282
- Section: Aluminum Alloys
- URL: https://journals.rcsi.science/0026-0673/article/view/235064
- DOI: https://doi.org/10.1007/s11041-016-0003-y
- ID: 235064
Cite item
Abstract
The effect of charge billet structure and form of fluxes on structure, density, and gas content of alloy AK6M2 (Al – Si – Cu system) is studied. Alloys prepared from finely crystalline charge billet have smaller phase component sizes, lower gas content, and increased solid state density, and use of coarsely crystalline charge billets for alloy preparation necessitates an increase in flux preparation consumption in the stage of alloy preparation for casting.
About the authors
K. V. Nikitin
Samara State Technical University
Author for correspondence.
Email: kvn-6411@mail.ru
Russian Federation, Samara
V. I. Nikitin
Samara State Technical University
Email: kvn-6411@mail.ru
Russian Federation, Samara
I. Yu. Timoshkin
Samara State Technical University
Email: kvn-6411@mail.ru
Russian Federation, Samara
O. A. Chikova
Ural Federal University named after the first President of Russia B. N. El’tsin
Email: kvn-6411@mail.ru
Russian Federation, Ekaterinburg
Supplementary files