FILLING OF CHANNELS OF THE ZEOLITE FRAMEWORK IN TRIGONAL POLAR NONABORATE Ва3Na0.9(OH)1.9[B9O16][B(OH)3]
- 作者: Topnikova A.1, Belokoneva E.1, Dimitrova O.1, Volkov A.1, Zorina L.2
-
隶属关系:
- Lomonosov Moscow State University, Moscow, 119991 Russia
- Osipyan Institute of Solid State Physics, Russian Academy of Sciences, Chernogolovka, Moscow region, 142432 Russia
- 期: 卷 68, 编号 2 (2023)
- 页面: 223-227
- 栏目: СТРУКТУРА НЕОРГАНИЧЕСКИХ СОЕДИНЕНИЙ
- URL: https://journals.rcsi.science/0023-4761/article/view/137365
- DOI: https://doi.org/10.31857/S0023476123020200
- EDN: https://elibrary.ru/BSWCKC
- ID: 137365
如何引用文章
详细
Crystals of the new trigonal borate Ва3Na0.9(OH)1.9[B9O16][B(OH)3] (sp. gr. P31c, a =10.23684(15) Å, c = 8.72926(13) Å) were prepared by the mild hydrothermal synthesis. The filling of the channels in the framework of the polar nonaborate was found to differ from that determined previously. It is consistent with the main features of this structure type with the preservation of sassoline molecules in the channels. The structure contains an additional ОН group, which is involved in the coordination of Ва.
作者简介
A. Topnikova
Lomonosov Moscow State University, Moscow, 119991 Russia
Email: nastya_zorina@rambler.ru
Россия, Москва
E. Belokoneva
Lomonosov Moscow State University, Moscow, 119991 Russia
Email: nastya_zorina@rambler.ru
Россия, Москва
O. Dimitrova
Lomonosov Moscow State University, Moscow, 119991 Russia
Email: nastya_zorina@rambler.ru
Россия, Москва
A. Volkov
Lomonosov Moscow State University, Moscow, 119991 Russia
Email: nastya_zorina@rambler.ru
Россия, Москва
L. Zorina
Osipyan Institute of Solid State Physics, Russian Academy of Sciences, Chernogolovka, Moscow region, 142432 Russia
编辑信件的主要联系方式.
Email: nastya_zorina@rambler.ru
Россия, Черноголовка
参考
- The Cambridge Crystallographic Data Centre (CCDC). Inorganic Crystal Structure Data Base – ICSD. https://www.ccdc.cam.ac.uk/, http://www.fiz-karlsruhe.de
- Crystallography Open Database. crystallography.net/cod
- Christ C.L., Clark J.R. // Phys. Chem. Miner. 1977. V. 2. P. 59.
- Liu L., Su X., Yang Y. et al. // Dalton Trans. 2014. V. 43. P. 8905.
- Smith R.W., Keszler D.A. // Mater. Res. Bull. 1989. V. 24. P. 725.
- Bubnova R.S., Krivovichev S.V., Filatov S.K. et al. // J. Solid State Chem. 2007. V. 180. P. 596.
- Белоконева Е.Л., Стефанович С.Ю., Димитрова О.В. // Кристаллография. 2012. Т. 57. С. 70.
- Wei Q., Sun L., Zhang J., Yang G.-Y. // Dalton Trans. 2017. V. 46. P. 7911.
- Heyward C., McMillen C.D., Kolis J. // J. Solid State Chem. 2013. V. 203. P. 166.
- Chen X., Wu L., Chang X., Xiao W. // Solid State Sci. 2014. V. 27. P. 47.
- Топникова А.П., Белоконева Е.Л. // Успехи химии. 2019. Т. 88. № 2. С. 204.
- Белоконева Е.Л., Стефанович С.Ю., Димитрова О.В. и др. // Кристаллография. 2009. Т. 54. № 5. С. 860.
- Agilent (2014). CrysAlis PRO. Agilent Technologies Ltd, Yarnton, Oxfordshire, England.
- Sheldrick G.M. // Acta Cryst. A. 2008. V. 64. P. 112.
- Farrugia L.J. // J. Appl. Cryst. 2012. V. 45. P. 849.
- Белоконева Е.Л., Стефанович С.Ю., Борисова Т.А., Димитрова О.В. // Журн. неорган. химии. 2001. Т. 46. С. 1788.
- Sheldrick G.M. // Acta Cryst. C. 2015. V. 71. P. 3.
- Dowty E. ATOMS. Shape Software, Kingsport, Tennessee, USA, 2006.
- Grube H.H. // Fortsch. Mineral. 1981. B. 59. S. 58.
- Lu J., Shi G., Wu H. et al. // RSC Adv. 2017. V. 7. P. 20259.
- Wu Ch., Song J., Li L. et al. // J. Mater. Chem. C. 2016. V. 4. P. 8189.
- Wei Q., Wang J.-J., He Ch. et al. // Chem. Eur. J. Commun. 2016. V. 22. P. 10759.
- Wu Ch., Jiang X., Lin L. et al. // Angew. Chem. Int. Ed. 2021. V. 60. № 52. P. 27151.