Morphology and spatial distribution of ordered domains in GaInP/GaAs(001) according to transmission electron microscopy

Capa

Citar

Texto integral

Acesso aberto Acesso aberto
Acesso é fechado Acesso está concedido
Acesso é fechado Somente assinantes

Resumo

The structure of epitaxial films of the GaInP solid solution, in which ordering occurs, was studied using transmission electron microscopy. The films were grown by metalorganic vapor phase epitaxy on GaAs (001) substrates near the half-composition point. During the study, dark-field images obtained using superstructure reflections for cross-sectional and plan-view specimens of films were analyzed. The morphology and relative spatial arrangement of ordered domains have been determined. The phenomenon of spontaneous self-organization of regions with CuPt–B+ and CuPt–B– ordering near the surface was discovered, while in the bulk of the film the domains are uniformly located and mutually overlap each other. The effect of spatial separation of domains is associated with the lattice relaxation, leading to a change in the surface topology.

Sobre autores

А. Myasoedov

Ioffe Institute RAS

Autor responsável pela correspondência
Email: amyasoedov88@gmail.com
Rússia, St. Petersburg

N. Bert

Ioffe Institute RAS

Email: amyasoedov88@gmail.com
Rússia, St. Petersburg

N. Kalyuzhnyy

Ioffe Institute RAS

Email: amyasoedov88@gmail.com
Rússia, St. Petersburg

A. Mintairov

Ioffe Institute RAS

Email: amyasoedov88@gmail.com
Rússia, St. Petersburg

Bibliografia

  1. Adachi S. Physical Properties of III–V Semiconductor Compounds. NY.: John Wiley & Sons, 1992. 13 p. https://doi.org/10.1002/352760281X
  2. Suzuki T. Basic Aspects of Atomic Ordering in III–V Semiconductor Alloys. NY.: Springer, 2002. 2 p. https://doi.org/10.1007/978-1-4615-0631-7_1
  3. Zunger A., Wood D.M. // J. Cryst. Growth. 1989. V. 98. № 1–2. P. 1. https://doi.org/10.1016/0022-0248(89)90180-2
  4. Srivastava G.P., Martins J.L., Zunger A. // Phys. Rev. B1985. V. 31. № 4. P. 2561. https://doi.org/10.1103/PhysRevB.31.2561
  5. Gomyo A., Suzuki T., Kobayashi K. et al. // Appl. Phys. Lett. 1987. V. 50. № 11. P. 673. https://doi.org/10.1063/1.98062
  6. Gomyo A., Suzuki T., Iijima S. // Phys. Rev. Lett. 1988. V. 60. № 25. P. 2645. https://doi.org/10.1103/PhysRevLett.60.2645
  7. Wei S.H., Laks D.B., Zunger A. // Appl. Phys. Lett. 1993. V. 62. № 16. P. 1937. https://doi.org/10.1063/1.109496
  8. Kurtz S.R. // J. Appl. Phys. 1993. V. 74. № 6. P. 4130. https://doi.org/10.1063/1.354437
  9. Froyen S., Zunger A., Mascarenhas A. // Appl. Phys. Lett. 1996. V. 68. № 20. P. 2852. https://doi.org/10.1063/1.116346
  10. Wei S.-H., Zhang S., Zunger A. // Jpn. J. Appl. Phys. 2000. V. 39. № S1. P. 237. https://doi.org/10.7567/jjaps.39s1.237
  11. Ponce F.A. // J. Phys. Conf. Ser. 2019. V. 1173. № 1. P. 012001. https://doi.org/10.1088/1742-6596/1173/1/012001
  12. Su P.Y., Liu H., Kawabata R.M.S. et al. // J. Appl. Phys. 2019. V. 125. № 5. P. 1. https://doi.org/10.1063/1.5063941
  13. Martín G., Coll C., López-Conesa L. et al. // ACS Appl. Electron. Mater. 2022. V. 4. № 7. P. 3478. https://doi.org/10.1021/acsaelm.2c00415
  14. Mintairov A.M., Kapaldo J., Merz J.L. et al. // Phys. Rev. B. 2017. V. 95. № 11. P. 1. https://doi.org/10.1103/PhysRevB.95.115442
  15. Mintairov A.M., Lebedev D.V., Bert N. et al. // Appl. Phys. Lett. 2019. V. 115. № 20. https://doi.org/10.1063/1.5126527
  16. Ahrenkiel S.P., Jones K.M., Matson R.J. et al. // MRS Proc. 1999. V. 583. P. 243. https://doi.org/10.1557/PROC-583-243
  17. Zhang S.B., Froyen S., Zunger A. // Appl. Phys. Lett. 1995. V. 67. P. 3141. https://doi.org/10.1063/1.114860
  18. Baxter C.S., Stobbs W.M., Wilkie J.H. // J. Cryst. Growth 1991. V. 112. № 2–3. P. 373. https://doi.org/10.1016/0022-0248(91)90313-T
  19. Bellon P., Chevalier J.P., Augarde E. et al. // J. Appl. Phys. 1989. V. 66. № 6. P. 2388. https://doi.org/10.1063/1.344245
  20. Nasi L., Salviati G., Mazzer M., Zanotti‐Fregonara C. // Appl. Phys. Lett. 1995. V. 68. P. 3263. https://doi.org/10.1063/1.116568
  21. Matthews J.W., Blakeslee A.E. // J. Cryst. Growth 1974. V. 27. P. 118. https://doi.org/10.1016/S0022-0248(74)80055-2
  22. Gutekunst G., Mayer J., Rühle M. // Philos. Mag. A. 1997. V. 75. № 5. P. 1329. https://doi.org/10.1080/01418619708209859
  23. Romanov A.E. // Int. J. Mater. Res. 2005. V. 96. № 5. P. 455. https://doi.org/doi.org/10.3139/ijmr-2005-0083
  24. Yastrubchak O., Wosinski T., Figielski T., Lusakowska E. // Physica E. 2003. V. 17. № 1–4. P. 561. https://doi.org/10.1016/S1386-9477(02)00871-8
  25. Zhang C.L., Xu B., Wang Z.G. et al. // Physica E. 2005. V. 25. № 4. P. 592. https://doi.org/10.1016/j.physe.2004.09.008

Declaração de direitos autorais © Russian Academy of Sciences, 2024

Este site utiliza cookies

Ao continuar usando nosso site, você concorda com o procedimento de cookies que mantêm o site funcionando normalmente.

Informação sobre cookies