Synthesis, X-ray structure analysis, and Raman spectroscopy of R2TiO5-based (R = Sc, Y) solid solutions

详细

Order–disorder transitions in xR₂O₃ · (1 − x)TiO₂ (R = Sc, 0.4 ≤ x ≤ 0.5; R = Y, 0.5 ≤ x ≤ 0.6) solid solutions with highly imperfect fluorite-derived structures have been studied using monochromatic synchrotron X-ray diffraction and Raman spectroscopy. The results demonstrate that the synthesis process leads to the formation of a fluorite-like (Fm3m) disordered phase and a nanoscale (~10–100 nm) pyrochlore-like (Fd3m) ordered phase of the same composition, coherent with the disordered phase. We have determined their lattice parameters. The Raman spectra of Sc₂TiO₅ (Y₂TiO₅) contain broad lines in low- and high-frequency regions: at 190, 350, and 775 (134, 188, 365, 404, and 727) cm⁻¹. These lines are characteristic of a pyrochlore-like phase with a varying degree of order and a disordered fluorite-like phase, respectively. The pyrochlore-like phase Y₂Ti₂O₇ has two strong Raman peaks in the low-frequency region: at 312 and 527 cm⁻¹. The formation of nanodomains with different degrees of order is caused by the internal stress that arises from the high density of structural defects in the unit cells of the solid solutions.