Preparation of High-Temperature Multicomponent Alloys by Mechanochemical Synthesis from Refractory Elements


Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Тек жазылушылар үшін

Аннотация

Highly dispersed powders of two-phase multicomponent alloys have been prepared by mechanochemical synthesis from Hf0.5Nb0.5Ta0.5Ti1.5Zr1 (composition 1) and HfNbTaTiZrMo (composition 2) refractory-metal mixtures in a Fritsch (P-7) planetary mill under an Ar atmosphere. Two solid solutions, with BCC and HCP lattices, were obtained from the five-component mixture (composition 1). In the case of the six-component mixture (composition 2), both solid solutions had BCC lattices. Using compaction by hot isostatic pressing at a temperature of 1200°C, we obtained dense samples. Mechanical tests in compression showed a combination of high strength and plasticity. For sample 1, we obtained a yield stress σy = 1317 MPa, compressive breaking stress σb = 1340 MPa, and relative breaking spread of 7%. Even better results were obtained for sample 2: σy = 2153 MPa and σb = 2165 MPa, with δ = 10%.

Авторлар туралы

V. Portnoi

Faculty of Chemistry, Moscow State University

Хат алмасуға жауапты Автор.
Email: valeri.portnoy@gmail.com
Ресей, Moscow, 119899

A. Leonov

Faculty of Chemistry, Moscow State University

Email: valeri.portnoy@gmail.com
Ресей, Moscow, 119899

M. Gusakov

OAO Kompozit

Email: valeri.portnoy@gmail.com
Ресей, Pionerskaya ul. 4, Korolev, Moscow oblast, 141074

I. Logachev

OAO Kompozit

Email: valeri.portnoy@gmail.com
Ресей, Pionerskaya ul. 4, Korolev, Moscow oblast, 141074

S. Fedotov

Dukhov All-Russia Research Institute of Automatics

Email: valeri.portnoy@gmail.com
Ресей, Sushchevskaya ul. 22, Moscow, 127055

Қосымша файлдар

Қосымша файлдар
Әрекет
1. JATS XML

© Pleiades Publishing, Inc., 2019