Photocatalytic activity of nanostructured titania coatings on aluminum substrates
- 作者: Baglov A.V.1, Denisov N.M.1, Borisenko V.E.1, Uglov V.V.2, Malashevich A.A.2
-
隶属关系:
- Belarussian State University of Informatics and Radioelectronics
- Belarussian State University
- 期: 卷 53, 编号 11 (2017)
- 页面: 1180-1184
- 栏目: Article
- URL: https://journals.rcsi.science/0020-1685/article/view/158324
- DOI: https://doi.org/10.1134/S0020168517110036
- ID: 158324
如何引用文章
详细
Titania coatings containing crystalline titania particles 10 to 20 and 100 to 300 nm in size or a combination of such particles have been produced by a sol–gel process on the surface of aluminum substrates. According to X-ray diffraction characterization results, the coatings consist predominantly of crystalline titania in the form of anatase. The decomposition of an organic test dye (Rhodamine B) in an aqueous solution under irradiation with UV light demonstrates that the highest photocatalytic activity is offered by the coatings containing both nanometer- and submicron-sized titania particles.
作者简介
A. Baglov
Belarussian State University of Informatics and Radioelectronics
编辑信件的主要联系方式.
Email: baglov@bsuir.by
白俄罗斯, vul. Browki 6, Minsk, 220013
N. Denisov
Belarussian State University of Informatics and Radioelectronics
Email: baglov@bsuir.by
白俄罗斯, vul. Browki 6, Minsk, 220013
V. Borisenko
Belarussian State University of Informatics and Radioelectronics
Email: baglov@bsuir.by
白俄罗斯, vul. Browki 6, Minsk, 220013
V. Uglov
Belarussian State University
Email: baglov@bsuir.by
白俄罗斯, pr. Nyezalyezhnastsi 4, Minsk, 220030
A. Malashevich
Belarussian State University
Email: baglov@bsuir.by
白俄罗斯, pr. Nyezalyezhnastsi 4, Minsk, 220030
补充文件