Microstructure and properties of α-tricalcium phosphate-based bone cement
- 作者: Fadeeva I.V.1, Filippov Y.Y.2, Fomin A.S.1, Petrakova N.V.1, Knotko A.V.2, Ryzhov A.P.1, Putlyaev V.I.2, Barinov S.M.1
-
隶属关系:
- Baikov Institute of Metallurgy and Materials Science
- Moscow State University
- 期: 卷 53, 编号 3 (2017)
- 页面: 292-299
- 栏目: Article
- URL: https://journals.rcsi.science/0020-1685/article/view/158187
- DOI: https://doi.org/10.1134/S0020168517030049
- ID: 158187
如何引用文章
详细
This paper examines the physicochemical properties and microstructure of brushite calcium phosphate cements possessing strength acceptable for application in surgery (15–20 MPa) and ensuring an optimal acidity (pH 6.5–7.5) of solutions in contact with them. Holding in a physiological saline produces significant changes in the microstructure of the cement relative to that before immersion in the solution: it causes a transformation of the most soluble components into platelike hydroxyapatite crystals.
作者简介
I. Fadeeva
Baikov Institute of Metallurgy and Materials Science
编辑信件的主要联系方式.
Email: fadeeva_inna@mail.ru
俄罗斯联邦, Leninskii pr. 49, Moscow, 119334
Ya. Filippov
Moscow State University
Email: fadeeva_inna@mail.ru
俄罗斯联邦, Moscow, 119991
A. Fomin
Baikov Institute of Metallurgy and Materials Science
Email: fadeeva_inna@mail.ru
俄罗斯联邦, Leninskii pr. 49, Moscow, 119334
N. Petrakova
Baikov Institute of Metallurgy and Materials Science
Email: fadeeva_inna@mail.ru
俄罗斯联邦, Leninskii pr. 49, Moscow, 119334
A. Knotko
Moscow State University
Email: fadeeva_inna@mail.ru
俄罗斯联邦, Moscow, 119991
A. Ryzhov
Baikov Institute of Metallurgy and Materials Science
Email: fadeeva_inna@mail.ru
俄罗斯联邦, Leninskii pr. 49, Moscow, 119334
V. Putlyaev
Moscow State University
Email: fadeeva_inna@mail.ru
俄罗斯联邦, Moscow, 119991
S. Barinov
Baikov Institute of Metallurgy and Materials Science
Email: fadeeva_inna@mail.ru
俄罗斯联邦, Leninskii pr. 49, Moscow, 119334
补充文件