High-temperature titanium nitridation kinetics
- 作者: Kovalev I.A.1, Kuznetsov K.B.1, Zufman V.Y.1, Ogarkov A.I.1, Shevtsov S.V.1, Kannykin S.V.2, Chernyavskii A.S.1, Solntsev K.A.1
-
隶属关系:
- Baikov Institute of Metallurgy and Materials Science
- Voronezh State University
- 期: 卷 52, 编号 12 (2016)
- 页面: 1230-1234
- 栏目: Article
- URL: https://journals.rcsi.science/0020-1685/article/view/158051
- DOI: https://doi.org/10.1134/S0020168516120050
- ID: 158051
如何引用文章
详细
Titanium samples 60.0 mm in length and 3.0 × 0.3 mm in cross section were heated in a nitrogen gas atmosphere for 60 min at temperatures from 1300 to 2100°C. At temperatures below 2000°C, the titanium nitridation process comprised two stages. The lower temperature limit of exponential nitridation kinetics was determined to be ~1000°C. At temperatures above the melting point of the metal, the presence of liquid phase in the bulk of the material has no significant effect on the titanium nitridation process.
作者简介
I. Kovalev
Baikov Institute of Metallurgy and Materials Science
Email: imet@imet.ac.ru
俄罗斯联邦, Leninskii pr. 49, Moscow, 119334
K. Kuznetsov
Baikov Institute of Metallurgy and Materials Science
Email: imet@imet.ac.ru
俄罗斯联邦, Leninskii pr. 49, Moscow, 119334
V. Zufman
Baikov Institute of Metallurgy and Materials Science
Email: imet@imet.ac.ru
俄罗斯联邦, Leninskii pr. 49, Moscow, 119334
A. Ogarkov
Baikov Institute of Metallurgy and Materials Science
编辑信件的主要联系方式.
Email: imet@imet.ac.ru
俄罗斯联邦, Leninskii pr. 49, Moscow, 119334
S. Shevtsov
Baikov Institute of Metallurgy and Materials Science
Email: imet@imet.ac.ru
俄罗斯联邦, Leninskii pr. 49, Moscow, 119334
S. Kannykin
Voronezh State University
Email: imet@imet.ac.ru
俄罗斯联邦, Universitetskaya pl. 1, Voronezh, 394018
A. Chernyavskii
Baikov Institute of Metallurgy and Materials Science
Email: imet@imet.ac.ru
俄罗斯联邦, Leninskii pr. 49, Moscow, 119334
K. Solntsev
Baikov Institute of Metallurgy and Materials Science
Email: imet@imet.ac.ru
俄罗斯联邦, Leninskii pr. 49, Moscow, 119334
补充文件