Structure and microwave dielectric properties of ZnTa2O6 ceramics with TiO2 and ZrO2 additions


如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

Ceramic samples based on ZnTa2O6 and ZnTa2O6–MO2 (M = Ti, Zr) systems have been obtained by the solid state ceramic route. The phase composition and microstructure of samples were investigated. The effect of the aliovalent substitution of ions Zn2+ and Ta5+ by M4+ (M = Ti, Zr) in the structure of ZnTa2O6 on microwave dielectric properties of ceramics was studied. The way of the compensation of the positive temperature coefficient of resonant frequency of dielectric resonators based on ZnTa2O6 ceramics with using the aliovalent substitution of cations was proposed. Dielectric resonators with the high temperature stability of the resonant frequency and high dielectric properties in the microwave range based on the ZnTa2O6–ZrO2 system were obtained for application in electronics.

作者简介

S. Redozubov

Giricоnd Research Institute; Ceramics Co. Ltd.

编辑信件的主要联系方式.
Email: s.s.redozubov@gmail.com
俄罗斯联邦, ul. Kurchatova 10, Saint-Petersburg, 194223; ul. Kurchatova 10, Saint-Petersburg, 194223

N. Kartenko

Ioffe Institute

Email: s.s.redozubov@gmail.com
俄罗斯联邦, Politechnicheskaya ul. 26, Saint-Petersburg, 194021

I. Gaidamaka

National Mineral Resources University

Email: s.s.redozubov@gmail.com
俄罗斯联邦, 21st Line 2, Saint-Petersburg, 199106

E. Nenasheva

Giricоnd Research Institute; Ceramics Co. Ltd.

Email: s.s.redozubov@gmail.com
俄罗斯联邦, ul. Kurchatova 10, Saint-Petersburg, 194223; ul. Kurchatova 10, Saint-Petersburg, 194223

补充文件

附件文件
动作
1. JATS XML

版权所有 © Pleiades Publishing, Ltd., 2016