Sintering and microstructure of materials based on the fluorohydroxyapatite–ZrO2–Al2O3 system

Abstract

We have studied the influence of the sintering temperature and modifying additives on the phase composition, microstructure, and mechanical strength of a fluorohydroxyapatite-based composite ceramic material containing 20 wt % zirconia. The addition of 5 wt % alumina has been shown to prevent recrystallization processes and contribute to phase composition stabilization. Moreover, the addition of a sintering aid (2 wt %) has made it possible to lower the sintering temperature to 1200°C and raise the bending strength of the material to 143 MPa.