EFFECT OF PRE-AGING ON THE THERMAL STABILITY OF ELECTRICAL CONDUCTIVITY AND MECHANICAL PROPERTIES OF THIN ALUMINUM WIRES Al–0.25%Zr–(Si, Er, Hf, Nb)

Iana S. Shadrina; Шадрина Яна Сергеевна; Aleksey V. Nokhrin; Нохрин Алексей Владимирович; Aleksandr A. Bobrov; Бобров Александр Андреевич; Nikolay N. Berendeev; Берендеев Николай Николаевич; Vladimir I. Kopylov; Копылов Владимир Ильич; Andrey V. Komel'kov; Комельков Андрей Вадимович; Mikhail K. Chegurov; Чегуров Михаил Константинович

doi:10.7868/S3034621525080105

EFFECT OF PRE-AGING ON THE THERMAL STABILITY OF ELECTRICAL CONDUCTIVITY AND MECHANICAL PROPERTIES OF THIN ALUMINUM WIRES Al–0.25%Zr–(Si, Er, Hf, Nb)

Authors: Shadrina I.S.¹, Nokhrin A.V.¹, Bobrov A.A.¹, Berendeev N.N.¹, Kopylov V.I.¹, Komel'kov A.V.¹, Chegurov M.K.¹
Affiliations:
1. National Research Lobachevsky State University of Nizhny Novgorod
Issue: Vol 126, No 8 (2025)
Pages: 922-935
Section: ПРОЧНОСТЬ И ПЛАСТИЧНОСТЬ
URL: https://journals.rcsi.science/0015-3230/article/view/286038
DOI: https://doi.org/10.7868/S3034621525080105
ID: 286038

Cite item

Full Text

Open Access
Restricted Access

Access granted
Restricted Access

Subscription Access

Abstract
About the authors
References
Supplementary files
Statistics

Abstract

The thermal stability of thin wires made of six aluminum alloys Al–0.25%Zr, additionally alloyed with Si, Er, Hf or Nb, has been studied. Aluminum alloy workpieces were obtained by induction casting, followed by stabilizing annealing (450°C, 1 h) and severe plastic deformation to fragmentation the cast structure. The wire with a diameter of 0.3 mm was made by drawing at room temperature. The thermal stability of the mechanical properties, microhardness, and specific electrical resistivity (SER) of stabilized aluminum wires has been studied. As the annealing temperature increases, a monotonous decrease in the tensile strength, microhardness, and SER of the wires occurs. It is established that the ductility of the wires
depends nonmonotonously (with a maximum) on the annealing temperature. The results of studies of the thermal stability of the properties of stabilized wires are compared with the characteristics of wires that have not been subjected to preliminary stabilizing annealing (450°C, 1 h).