Crack resistance of maraging steel at cyclic loading

封面

如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

The effect of the structure on the strength and crack resistance of maraging steel is studied at cyclic loading. The impact of dispersity of intermetallide precipitates formed during tempering on the cyclic crack resistance is considered. The paper discusses the variation in the characteristics of cyclic crack resistance of the studied steel depending on the elements of its microstructure and on the modes of quenching and ubsequent tempering. It is shown that in a maraging steel with a coarse-grained structure, there is a high level of near-threshold cyclic crack resistance, probably related with the ratio of the number of loading cycles and the size of the cyclic plastic deformation zone.

作者简介

Yu. Simonov

Perm National Research Polytechnic University

Email: akalet@imp.uran.ru
俄罗斯联邦, Perm, 614990

M. Simonov

Perm National Research Polytechnic University

Email: akalet@imp.uran.ru
俄罗斯联邦, Perm, 614990

Yu. Kaletina

Mikheev Institute of Metal Physics, Ural Branch, Russian Academy of Sciences

Email: akalet@imp.uran.ru
俄罗斯联邦, Ekaterinburg, 620108

A. Kaletin

Mikheev Institute of Metal Physics, Ural Branch, Russian Academy of Sciences

编辑信件的主要联系方式.
Email: akalet@imp.uran.ru
俄罗斯联邦, Ekaterinburg, 620108

参考

  1. He Y., Yang K., Sha W., Cleland D.J. Microstructure and mechanical properties of a 2000 MPa Co-free maraging steel after aging at 753 K // Metall. Mater. Trans. A. 2004. V. 35. № 9. P. 2747–2755.
  2. Wang W., Yan W., Duan Q., Shan Y., Zhang Z., Yang K. Study on fatigue property of a new 2.8 GPa grade maraging steel // Mater. Sci. Eng. A. 2010. V. 527. P. 3057–3063.
  3. Tariq F., Naz N., Baloch R.A. Effect of cycling aging on mechanical properties and microstructure of maraging steel 250 // J. Mater. Eng. Perf. (JMEP). 2010. V. 19. P. 1005–1014.
  4. Hou H., Li H.F., Jin Y.C., Wang X.R., Wen Z.Q. Effect of heat treatment temperature on the mechanical properties of low-temperature high strength maraging steel // Mater. Sci. Eng. A. 2014. V. 601. P. 1–6.
  5. Wang B., Duan Q.Q., Zhang P., Zhang Z.J., Li Z.F., Zhang X.W. Investigation on the cracking resistances of different ageing treated 18Ni maraging steels // Mater. Sci. Eng. A. 2020. V. 771. P. 138553.
  6. Xu Z.K., Wang B., Zhang P., Zhang Z.F. Short fatigue crack growth behavior in 18Ni maraging steel // Mater. Sci. Eng. A. 2021. V. 807. P. 140844.
  7. Zhang Z., Koyama M., Tsuzaki K., Noguchi H. Three-dimensional characterization of low-cycle fatigue crack morphology in TRIP-maraging steel: Crack closure, geometrical uncertainty and wear // Intern. J. Fatigue. 2021. V. 143. P. 106032.
  8. Zhang C., Wang C., Zhang S.L., Ding Y.L., Ge Q.L., Su J. Effect of aging temperature on the precipitation behavior and mechanical properties of Fe-Cr-Ni maraging stainless steel // Mater. Sci. Eng. A. 2021. V. 806. P. 140763.
  9. Li H., Liu Y., Liu B., Wei D.X. Synergistic enhancement of strength and ductility of cobalt-free maraging steel via nanometer-scaled microstructures // Mater. Sci. Eng. A. 2022. V. 842. P. 143099.
  10. Li J.H., Zhan D.P., Jiang Z.H., Zhang H.S., Yang Y.K., Zhang Y.P. Progress on improving strength-toughness of ultra-high strength martensitic steels for aerospace applications: a review // J. Mater. Research Techn. 2023. V. 23. № 3–4. P. 172–190.
  11. Rosenauer A., Brandl D., Ressel G., Lukas S., Monschein S., Stockinger M., Schnitzer R. Influence of delta ferrite on the impact toughness of a PH 13-8 Mo maraging steel // Mater. Sci. Eng. A-Struct. Mater. Prop. Microstruct. Process. 2022. V. 856. P. 144024.
  12. Симонов Ю.Н., Симонов М.Ю., Калетина Ю.В., Калетин А.Ю. Структура и трещиностойкость мартенситностареющих сталей при однократном нагружении // ФММ. 2023. Т. 124. № 10. С. 978–987.
  13. Paris P.C., Erdogan F.A. Critical Analysis of Crack Propagation Laws // J. Basic Eng. 1963. V. 85. P. 528–533.
  14. Elber W. The Significance of Fatigue Crack Closure. In: Rosenfeld, M. Ed. Damage Tolerance in Aircraft Structures, ASTM International, West Conshohocken, PA. 1971. P. 230–242.
  15. Ritchie R.O., Suresh S. Some considerations on fatigue crack closure at near-threshold stress intensities due to fracture surface morphology // Met. Trans. 1982. V. 13A. № 5. P. 937–940.
  16. Романив О.Н., Никифорчин Г.Н., Студент А.З., Цирульник А.Т. О двух особенностях оценки коррозионной трещиностойкости конструкционных сплавов // ФХММ. 1982. Т. 16. № 1. С. 35–47.
  17. Георгиев М., Межова Н. Приложна механика на разрушаването. София: Булвест 2000, 2013. 559 с.
  18. Yoder G.R., Cooley L.A., Crooker T.W. Quantitative analysis of microstructural effects on fatigue crack growth in widmastatten Ti–6Al–4V and Ti–8Al–1Mo–1V // Eng. Fract. Mech. 1979. V. 11. № 4. P. 805–816.
  19. Симонов Ю.Н. Структурные аспекты прочности и трещиностойкости низкоуглеродистых конструкционных сталей / Дис. д-ра техн. наук. Пермь: ПГТУ, 2004. 383 с.
  20. Hornbogen E., Zumhgar K-H. Microstructure and fatigue crack growth in a γ-Fe–Ni–Al alloy // Acta Met. 1976. V. 24. № 6. P. 581–592.

补充文件

附件文件
动作
1. JATS XML
下载


Согласие на обработку персональных данных с помощью сервиса «Яндекс.Метрика»

1. Я (далее – «Пользователь» или «Субъект персональных данных»), осуществляя использование сайта https://journals.rcsi.science/ (далее – «Сайт»), подтверждая свою полную дееспособность даю согласие на обработку персональных данных с использованием средств автоматизации Оператору - федеральному государственному бюджетному учреждению «Российский центр научной информации» (РЦНИ), далее – «Оператор», расположенному по адресу: 119991, г. Москва, Ленинский просп., д.32А, со следующими условиями.

2. Категории обрабатываемых данных: файлы «cookies» (куки-файлы). Файлы «cookie» – это небольшой текстовый файл, который веб-сервер может хранить в браузере Пользователя. Данные файлы веб-сервер загружает на устройство Пользователя при посещении им Сайта. При каждом следующем посещении Пользователем Сайта «cookie» файлы отправляются на Сайт Оператора. Данные файлы позволяют Сайту распознавать устройство Пользователя. Содержимое такого файла может как относиться, так и не относиться к персональным данным, в зависимости от того, содержит ли такой файл персональные данные или содержит обезличенные технические данные.

3. Цель обработки персональных данных: анализ пользовательской активности с помощью сервиса «Яндекс.Метрика».

4. Категории субъектов персональных данных: все Пользователи Сайта, которые дали согласие на обработку файлов «cookie».

5. Способы обработки: сбор, запись, систематизация, накопление, хранение, уточнение (обновление, изменение), извлечение, использование, передача (доступ, предоставление), блокирование, удаление, уничтожение персональных данных.

6. Срок обработки и хранения: до получения от Субъекта персональных данных требования о прекращении обработки/отзыва согласия.

7. Способ отзыва: заявление об отзыве в письменном виде путём его направления на адрес электронной почты Оператора: info@rcsi.science или путем письменного обращения по юридическому адресу: 119991, г. Москва, Ленинский просп., д.32А

8. Субъект персональных данных вправе запретить своему оборудованию прием этих данных или ограничить прием этих данных. При отказе от получения таких данных или при ограничении приема данных некоторые функции Сайта могут работать некорректно. Субъект персональных данных обязуется сам настроить свое оборудование таким способом, чтобы оно обеспечивало адекватный его желаниям режим работы и уровень защиты данных файлов «cookie», Оператор не предоставляет технологических и правовых консультаций на темы подобного характера.

9. Порядок уничтожения персональных данных при достижении цели их обработки или при наступлении иных законных оснований определяется Оператором в соответствии с законодательством Российской Федерации.

10. Я согласен/согласна квалифицировать в качестве своей простой электронной подписи под настоящим Согласием и под Политикой обработки персональных данных выполнение мною следующего действия на сайте: https://journals.rcsi.science/ нажатие мною на интерфейсе с текстом: «Сайт использует сервис «Яндекс.Метрика» (который использует файлы «cookie») на элемент с текстом «Принять и продолжить».