Highly efficient dye-sensitized solar cell prepared by electrophoretic deposition method: the effect of TiO2 films thickness on the performance of cells

Аннотация

In this work, nanocrystalline P25 TiO₂ films with different thicknesses were deposited on FTO coated glass substrates by an electrophoretic deposition technique (EPD) and applied as the work electrode for dye-sensitized solar cells (DSSC) using cis-bis(isothiocyanato)(2,2'-bipyridyl-4,4'-dicarboxylato)(4,4'di-nonyl-2'-bipyridyl) ruthenium(II) (Z907, Dyesol) as sensitizing dye.The results showed that the increasing the thickness of TiO₂ films lead to increase the adsorption of the dye on the TiO₂ layers which in turns improved the short-circuit photocurrent (J_sc) and open-circuit voltage (V_oc), respectively. Furthermore, it was found that the effects of the surface states on the recombination of the photo-injected electrons (electron–hole pairs) in the TiO₂ films strongly depend on theTiO₂ electrode annealing temperature. Finally, a DSSC with a 32.82 μm thickness for TiO₂ film annealed at 600°C produced the highest conversion efficiency with an incident solar energy of 100 mW/cm² (η = 8.23%, J_sc = 15.98, V_oc = 0.73, FF = 0.7).