Nanostructured Zirconia Ceramic Based on Baddeleyite Domestic Raw
- Autores: Zhigachev A.O.1, Golovin Y.I.1,2
-
Afiliações:
- Tambov State University
- Moscow State University
- Edição: Volume 12, Nº 7-8 (2017)
- Páginas: 400-408
- Seção: Article
- URL: https://journals.rcsi.science/2635-1676/article/view/220086
- DOI: https://doi.org/10.1134/S1995078017040176
- ID: 220086
Citar
Resumo
The relationship between synthesis conditions, structure, and properties of baddeleyite-based engineering nanostructured zirconia ceramics is studied in this work. Mined at the Kovdor beneficiation plant (Murmansk oblast), baddeleyite is a domestic material that is much cheaper when compared to its analogue, synthetic ZrO2, conveniently used in the production of zirconia ceramics. Zirconia ceramic with a grain size of 100–150 nm and a relative density of above 99% is fabricated, wherein a high hardness (13.3 GPa) and a fracture toughness (13.2 MPa m0.5) are combined.
Sobre autores
A. Zhigachev
Tambov State University
Autor responsável pela correspondência
Email: andreyzhig2009@gmail.com
Rússia, Tambov, 392000
Yu. Golovin
Tambov State University; Moscow State University
Email: andreyzhig2009@gmail.com
Rússia, Tambov, 392000; Moscow, 119991
Arquivos suplementares