Kinetics of α’-phase nucleation during thermal aging of Fe–22% Cr alloy
- Авторлар: Rogozhkin S.1,2, Korchuganova O.1,2, Aleev A.1,2
-
Мекемелер:
- National Research Nuclear University Moscow Engineering Physics Institute
- Institute for Theoretical and Experimental Physics
- Шығарылым: Том 7, № 2 (2016)
- Беттер: 210-213
- Бөлім: Materials of Power Engineering and Radiation-Resistant Materials
- URL: https://journals.rcsi.science/2075-1133/article/view/204934
- DOI: https://doi.org/10.1134/S2075113316020179
- ID: 204934
Дәйексөз келтіру
Аннотация
The initial stage of phase separation of binary Fe–22 at % Cr alloy during thermal aging at 500°C is studied at the atomic-scale level by atom probe tomography. Upon the behavior analysis of pair-correlation function of chromium atoms, long-range correlations typical of spinodal decomposition are observed at short aging times, which disappear 25 h after aging. The analysis of 3D atomic maps shows that Cr-rich regions form at the initial steps of decomposition, where the chromium concentration increases with an increase in the aging time. At the aging time of ~100 h, the chromium concentration in the center of these regions reaches 80 at %, which corresponds to the α' phase.
Негізгі сөздер
Авторлар туралы
S. Rogozhkin
National Research Nuclear University Moscow Engineering Physics Institute; Institute for Theoretical and Experimental Physics
Хат алмасуға жауапты Автор.
Email: SVRogozhkin@mephi.ru
Ресей, Kashirskoe sh. 31, Moscow, 115409; ul. B. Cheremushkinskaya 25, Moscow, 117218
O. Korchuganova
National Research Nuclear University Moscow Engineering Physics Institute; Institute for Theoretical and Experimental Physics
Email: SVRogozhkin@mephi.ru
Ресей, Kashirskoe sh. 31, Moscow, 115409; ul. B. Cheremushkinskaya 25, Moscow, 117218
A. Aleev
National Research Nuclear University Moscow Engineering Physics Institute; Institute for Theoretical and Experimental Physics
Email: SVRogozhkin@mephi.ru
Ресей, Kashirskoe sh. 31, Moscow, 115409; ul. B. Cheremushkinskaya 25, Moscow, 117218