Email this article Austenite in Nanostructured Maraging Steel
- Authors: Sukhikh A.A.1, Makhneva T.M.1, Dement’ev V.B.1
-
Affiliations:
- Udmurt Federal Research Center, Ural Branch, Russian Academy of Sciences
- Issue: Vol 10, No 4 (2019)
- Pages: 966-973
- Section: Article
- URL: https://journals.rcsi.science/2075-1133/article/view/208036
- DOI: https://doi.org/10.1134/S2075113319040415
- ID: 208036
Cite item
Open Access
Access granted
Subscription Access
Abstract
Abstract—The structural formation and properties of austenite in martensite aged (maraging) 03N18K9M5T steel were analyzed. The morphological features of austenite, determining its resilience to heating, supercooling, and plastic deformation, were established. The difference between the characteristics of residual and reverted austenite was substantiated. The contributions of phase hardening and dispersion of crystals to the yield strength of residual austenite were determined. The role of both types of austenite in the formation of steel was shown as well.
About the authors
A. A. Sukhikh
Udmurt Federal Research Center, Ural Branch, Russian Academy of Sciences
Email: mah@udman.ru
Russian Federation, Izhevsk
T. M. Makhneva
Udmurt Federal Research Center, Ural Branch, Russian Academy of Sciences
Author for correspondence.
Email: mah@udman.ru
Russian Federation, Izhevsk
V. B. Dement’ev
Udmurt Federal Research Center, Ural Branch, Russian Academy of Sciences
Email: mah@udman.ru
Russian Federation, Izhevsk
Supplementary files