Synthesis and Electrochemical Properties of Lithium Titanate


Citar

Texto integral

Acesso aberto Acesso aberto
Acesso é fechado Acesso está concedido
Acesso é fechado Somente assinantes

Resumo

The synthesis of lithium titanate which includes mechanical activation of the precursor on a Bridgman anvil high-pressure apparatus is proposed. The electrodes composed of the prepared Li4Ti5O12 surpass their analogs in terms of the charge density, especially at high discharge currents, which we attribute to considerably finer particles of the prepared active material and the use of a solid polymer electrolyte as an electrically conducting binder which ensures uniform accessibility of the surface of anode material particles. This results in the most complete involvement of the lithium titanate during charge–discharge cycles and, consequently, higher specific discharge capacity. Solid state electrodes offer the advantage of stability, as compared to other electrodes, due to the lack of a liquid electrolyte in their composition; liquid electrolytes are known to cause corrosion, which leads to substantial losses of the electrode capacity during charge–discharge cycles.

Sobre autores

S. Smirnov

National Research University Moscow Power Engineering Institute

Autor responsável pela correspondência
Email: sesmirnov53@mail.ru
Rússia, Moscow, 111250

V. Zhorin

Semenov Institute of Chemical Physics

Email: sesmirnov53@mail.ru
Rússia, Moscow, 119991

M. Kiselev

Frumkin Institute of Physical Chemistry and Electrochemistry

Email: sesmirnov53@mail.ru
Rússia, Moscow, 119991

S. Smirnov

National Research University Moscow Power Engineering Institute

Email: sesmirnov53@mail.ru
Rússia, Moscow, 111250

N. Yashtulov

Moscow Technological University

Email: sesmirnov53@mail.ru
Rússia, Moscow, 119571

Arquivos suplementares

Arquivos suplementares
Ação
1. JATS XML

Declaração de direitos autorais © Pleiades Publishing, Ltd., 2018