Investigation of aluminum–copper bimetal-based intermetallide coating produced by contact melting method
- Авторы: Pronichev D.V.1, Gurevich L.M.1, Trykov Y.P.1, Trunov M.D.1
-
Учреждения:
- Volgograd State Technical University
- Выпуск: Том 7, № 1 (2016)
- Страницы: 97-101
- Раздел: Article
- URL: https://journals.rcsi.science/2075-1133/article/view/204709
- DOI: https://doi.org/10.1134/S2075113316010226
- ID: 204709
Цитировать
Аннотация
An explosive-welded copper–aluminum composite was heat-treated at 570°C. The microhardness, chemical composition, and electrical conductance of the composite were investigated before and after thermal treatment.
Ключевые слова
Об авторах
D. Pronichev
Volgograd State Technical University
Автор, ответственный за переписку.
Email: mv@vstu.ru
Россия, pr. Lenina 28, Volgograd, 400066
L. Gurevich
Volgograd State Technical University
Email: mv@vstu.ru
Россия, pr. Lenina 28, Volgograd, 400066
Yu. Trykov
Volgograd State Technical University
Email: mv@vstu.ru
Россия, pr. Lenina 28, Volgograd, 400066
M. Trunov
Volgograd State Technical University
Email: mv@vstu.ru
Россия, pr. Lenina 28, Volgograd, 400066
Дополнительные файлы