Influence of Dew Point on the Selective Oxidation, Microstructure and Mechanical Properties of a High-Al Low-Si Dual Phase Steel during Hot-Dip Galvanizing Process

Resumo

The effect of dew point on the selective oxidation behavior, microstructure and mechanical properties of a high-Al low-Si dual phase steel is elucidated. The results showed that as dew point is increased from–30°C to +5°C, internal oxidation of alloying elements occurs, and consequently the mass of external oxides decreases, which improves the galvanisability of steel sheets. It was also observed that the dew point had an impact on the microstructure and mechanical properties of the experimental steel. With the increase of dew point, the decarburization layer on the surface was increased, leading to inferior mechanical properties. Compared with the industrial steel, the high-Al-low-Si DP steel exhibited excellent galvanisability under identical annealing conditions.