Effect of SO42-, Cl– and NO3- anions on the formation of iron oxide nanoparticles via microwave synthesis

Resumo

In the present work iron oxide nanoparticles have been prepared by microwave assisted synthesis with the influence of different precursor salts and synthesis of magnetite, hematite, Iron oxide hydroxide and maghemite nanoparticles. Synthesized iron oxide nanoparticles were characterized with Infrared Spectroscopy (FTIR), Field Emission Scanning Electron Microscopy (FESEM), and Energy-dispersive X-ray Spectroscopy (EDX). XRD measurements show that the peaks of diffractogram are in agreement with the theoretical data of magnetite, hematite, FeO(OH) (Iron oxide hydroxide) and maghemite. Crystallite size of the particles was found to be 33, 45, 36 and 43.5 nm for Fe₃O₄, α-Fe₂O₃, FeO(OH) and γ-Fe₂O₃. FESEM studies indicated that size of the particles is observed in the range of about 19.4 to 46.7 nm (Fig. 2a, average 32 nm), 29.1 to 67.6 nm (Fig. 2b average 45 nm), 29.1 to 40.8 (Fig. 2c average 36.6 nm), 29.1 to 80 nm (Fig. 2d average 43.5) for Fe₃O₄, α-Fe₂O₃, FeO(OH) and γ-Fe₂O₃ respectively. EDX spectral analysis reveals the presence of carbon, oxygen, iron in the synthesized nanoparticles. The FTIR graphs indicated absorption bands due to O–H stretching, C–O bending, C–H stretching and Fe–O stretching vibrations.