Hydrocracking of vegetable oil on boron-containing catalysts: Effect of the nature and content of a hydrogenation component

详细

Catalysts based on metals (Pt, Pd) and metal oxides (NiO, Co₃O₄, MoO₃, WO₃), supported on the surface of borate-containing aluminum oxide (B₂O₃–Al₂O₃), in the hydrocracking of sunflower oil at a temperature of 400°C, a pressure 4.0 MPa and a mass hourly space velocity MHSV 5.0 h^–1 are compared. H₂ TPR and IR spectroscopy of adsorbed CO and ESDR show that the hydrogenation catalyst components are Pt⁰ and Pd⁰, a mixture of Ni²⁺ + Ni⁰, Co²⁺ + Co⁰, or a mixture of the highest and partially reduced oxides of Mo and W. It is established that catalysts containing Pt, Pd, NiO and Co₃O₄, ensure complete oil hydrodeoxygenation. The main oxygen removal reactions in Ptand Pd-systems are decarboxylation and hydrodecarbonylation. For catalysts with NiO and Co₃O₄, characteristic reactions are reduction and methanation. The highest yield of the diesel fraction was obtained on Pt/B₂O₃-Al₂O₃ catalysts with metal contents of 0.3–1.0 wt %. Along with n-alkanes, the diesel fractions obtained on these catalysts include cycloalkanes and iso-alkanes (up to around 40 wt %) and aromatic hydrocarbons present in trace amounts. Hydrocracking on the Pt system at 400°C for 20 h with MHSV of 1.0 h^–1 produces a diesel fraction with a yield of at least 82.0 wt % and the content of iso-alkanes at least 76.1 wt %.