Influence of Matrix Nature on the Structural Characteristics of In2O3–CeO2 and SnO2–CeO2 Composites Fabricated by the Impregnation Method

Resumo

The structural characteristics, valence states, and distribution of cerium ions between the components in In₂O₃–CeO₂ and SnO₂–CeO₂ nanocomposites fabricated using the impregnation method were studied. X-ray photoelectron spectroscopy (XPS) and energy-dispersive X-ray spectroscopy (EDX) were used to show that, during impregnation, cerium ions are not included into In₂O₃ crystals and are disposed only on their surface in the form of nano-sized crystallites or amorphous clusters. On the other side, under the contact of CeO₂ clusters with a surface of SnO₂ matrix crystals, cerium ions penetrate into the surface layer of these crystals. In contrast to an In₂O₃–CeO₂ system, where the addition of CeO₂ does not affect the conduction activation energy, where cerium oxide is added to SnO₂, the observed increase in the resistance of a SnO₂–CeO₂ composite is accompanied by a sufficient increase in activation energy. These data and the XPS spectra confirm the modification of the surface layers of conductive SnO₂ crystals as, a result of the penetration of cerium ions into these layers.