Email this article Anotherdate base material "Ftoraks", covered with silicon carbide
- Authors: Voronov I.A.1
-
Affiliations:
- A.I. Evdokimov Moscow state medical-dental University
- Issue: Vol 20, No 1 (2016)
- Pages: 4-6
- Section: Articles
- URL: https://journals.rcsi.science/1728-2802/article/view/42014
- DOI: https://doi.org/10.18821/1728-28022016;20(1):4-6
- ID: 42014
Cite item
Full Text
Abstract
Taking into account that the coating «Pantsyr» is a thin layer of film coating of silicon carbide, to study its hardness was used scanning nanohardness «NanoScan-3D». To study our nanohardness coating samples were produced from plastic «Ftoraks», half of which was coated with a thickness of 1600 nm. Measurements were carried out in 5 randomly selected points on the surface of the plastic samples uncoated and coated with a load on the indenter 1 mN. V result of the study sample nanohardness bases dentures made ofplastic «Ftoraks» uncoated and ion-plasma silicon carbide-coated «Pantsyr» with the help of apparatus «Nano Scan 3D» we are under a load of 1 mN to the indenter, we found that the parameters of the samples nanohardness bases after coating «Pantsyr» increased 1.4 times, reaching values of 310±9 MPa. This result indicates a significant hardening of the surface of the denture base that provides apparently and high wear resistance.
Keywords
Full Text
##article.viewOnOriginalSite##About the authors
Igor' Anatol'evich Voronov
A.I. Evdokimov Moscow state medical-dental University
Email: voronov77@mail.ru
Department of integrated prosthetics; implant surgeon, orthopedist, candidate of medical Sciences, corresponding member of Academy of medical and technical Sciences 127206, Moscow
References
- Хрущев М.М. Трение, износ и микротвердость материалов: Избранные работы (к 120-летию со дня рождения) / Отв. ред. И.Г. Горячева. М.: КРАСАД; 2012.
- ГОСТ 9450-76. Измерение микротвердости вдавливанием алмазных наконечников. Введен 1977-01-01. М.: Издательство стандартов; 1976.
- Oliver W.C., Pharr G.M. An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J. Mater. Res. 1992; 7 (06): 1564-83.
- Oliver W.C., Pharr G.M. Measurement of hardness and elastic modulus by instrumented indentation: Advances in understanding and refinements to methodology. J. Mater. Res. 2004; 19 (01): 3-20.
Supplementary files