Physical–chemical properties and conductivity of Na2O–SnO2–SiO2 glass systems
- 作者: Kovyazina I.1, Nechaev G.2, Vlasova S.1, Reznitskikh O.2
-
隶属关系:
- Ural Federal University
- Institute of High-Temperature Electrochemistry, Ural Branch
- 期: 卷 43, 编号 2 (2017)
- 页面: 146-150
- 栏目: Article
- URL: https://journals.rcsi.science/1087-6596/article/view/215932
- DOI: https://doi.org/10.1134/S1087659617020080
- ID: 215932
如何引用文章
详细
The effect of tin(IV) oxide on the conductivity and chemical stability of sodium–silicate glass has been studied for five different glass compositions. Dilatometry and DSC were used to investigate the thermal behavior of the glass. The research into transport characteristics of the glass has shown that its conductivity is in the range of 2 × 10–8–5 × 10–7 S/cm at 25°C and 10–3 S/cm at 300°C.
作者简介
I. Kovyazina
Ural Federal University
Email: N_gregory@mail.ru
俄罗斯联邦, Yekaterinburg, 620002
G. Nechaev
Institute of High-Temperature Electrochemistry, Ural Branch
编辑信件的主要联系方式.
Email: N_gregory@mail.ru
俄罗斯联邦, Yekaterinburg, 620137
S. Vlasova
Ural Federal University
Email: N_gregory@mail.ru
俄罗斯联邦, Yekaterinburg, 620002
O. Reznitskikh
Institute of High-Temperature Electrochemistry, Ural Branch
Email: N_gregory@mail.ru
俄罗斯联邦, Yekaterinburg, 620137